原位插层聚合法制备聚苯乙烯-蒙脱土纳米复合材料  

STUDY ON POLYSTYRENE-MONTMORILLONITE NANOCOMPOSITES

作　　者：金星[1] 戚嵘嵘[1] 周持兴[1] 

机构地区：[1]上海交通大学化学化工学院,上海200240

出　　处：《高分子材料科学与工程》2005年第4期105-108,共4页Polymer Materials Science & Engineering

基　　金：国家自然科学基金重大项目资助(50390095)

摘　　要：采用双-苯基二甲基十八烷基溴化铵(TBDO)作为有机插层剂对钠基蒙脱土进行了有机化处理,该有机化的蒙脱土粒子在苯乙烯单体中很容易地均匀分散并形成稳定的胶体溶液。通过对分散有蒙脱土的苯乙烯进行自由基聚合制备了聚苯乙烯-蒙脱土纳米复合材料,X射线衍射和透射电镜研究表明形成了原位插层型和部分插层部分剥离型纳米复合材料。该纳米复合材料与同法制备的纯聚苯乙烯相比,具有更高的分子量(M-w),较低的玻璃化转变温度(Tg)和优良的热稳定性。Polystyrene-MMT nanocomposites were prepared by free radical polymerization of styrene containing dispersed clay. The organophilic MMT particles were easily dispersed and swollen in styrene monomer. The intercalation spacing in the nanocomposites and the degree of dispersion of these composites were investigated by X-ray diffraction and transmission electron microscopy, respectively. The nanocomposites have higher molecular weight (_w), lower T_g and better thermal stability compared to the virgin polystyrene.

关 键 词：聚苯乙烯 蒙脱土 纳米复合材料 自由基聚合 

分 类 号：TB383[一般工业技术—材料科学与工程]