Synthesis of Y_2O_3 Nano-Powder from Yttrium Oxalate under Ambient Temperature  

作　　者：李玲 

机构地区：[1]Department of Physics, Jinan University, Guangzhou 510632, China

出　　处：《Journal of Rare Earths》2005年第3期358-361,共4页稀土学报（英文版）

基　　金：theScientificandTechnologicalPlanofGuangdongProvince (2 0 0 2C10 3 0 40 2 )andKeySubjectofScientificandTechnologicalPlanofGuangzhouCity (2 0 0 2Z2 2 0 2 3 )

摘　　要：High purity Y_2O_3 nano-powders was synthesized directly from solution ofindustrial YCl_3 by method of oxalate precipitation through super-micro-reactors made by complexnon-ionic surfactant. The purity and diameter of Y_2O_3 particles were controlled by such processingparameters as concentration of YCl_3 and oxalic acid and complex non-ionic surfactant etc. TEMphotomicrographs show that Y_2O_3 particles are spherical in shape, with an average diameter of lessthan 30 nm. Test results certify that the purity and particle diameter as well as the dispersion ofY_2O_3 nano-powder depend on the concentrations of YCl_3, oxalic acid and complex non-ionicsurfactant. The optimum ranges of the concentrations for YCl_3 and complex non-ionic surfactant whenthe diameter of Y_2O_3 particles is smaller than 100 nm are 0.43 ～1.4 mol ? L^(-1) and0.031～0.112 mol·L^(-1) respectively, while the mass fraction range of oxalic acid is 10% ～18% .The purity of Y_2O_3 nano-powder tested by ICP-AES analysis is 99.99% .High purity Y_2O_3 nano-powders was synthesized directly from solution ofindustrial YCl_3 by method of oxalate precipitation through super-micro-reactors made by complexnon-ionic surfactant. The purity and diameter of Y_2O_3 particles were controlled by such processingparameters as concentration of YCl_3 and oxalic acid and complex non-ionic surfactant etc. TEMphotomicrographs show that Y_2O_3 particles are spherical in shape, with an average diameter of lessthan 30 nm. Test results certify that the purity and particle diameter as well as the dispersion ofY_2O_3 nano-powder depend on the concentrations of YCl_3, oxalic acid and complex non-ionicsurfactant. The optimum ranges of the concentrations for YCl_3 and complex non-ionic surfactant whenthe diameter of Y_2O_3 particles is smaller than 100 nm are 0.43 ～1.4 mol ? L^(-1) and0.031～0.112 mol·L^(-1) respectively, while the mass fraction range of oxalic acid is 10% ～18% .The purity of Y_2O_3 nano-powder tested by ICP-AES analysis is 99.99% .

关 键 词：oxalate precipitation method complex non-ionic surfactant super-micro-reactor Y_2O_3 nano-powder synthesis rare earths 

分 类 号：O614.322[理学—无机化学]