热致液晶共聚酯／Nylon－1010共混物的研究  

A STUDY ON BLENDS BASED ON THERMOTROPIC LIQUID CRYSTAL COPOLYESTER AND NYLON-1010

作　　者：王尚尔[1] 郭颖志[1] 倪玉山[1] 莫志深[1] 牟忠诚[1] 

机构地区：[1]中国科学院长春应用化学研究所高分子物理开放实验室,东北师范大学分析测试中心

出　　处：《高分子学报》1995年第3期302-307,共6页Acta Polymerica Sinica

基　　金：国家自然科学基金

摘　　要：利用偏光显微镜（ＰＬＭ），差示扫描量热计及广角Ｘ－射线衍射等手段研究了热致液晶共聚酯／Ｎｙｌｏｎ－１０１０共混体系．发现当热致液晶共聚酯（ＨＴＨ１０）含量达到３０％时共混物微结构与纯ＨＴＨ１０相似．尼龙－１０１０的结晶度先是随ＨＴＨ１０含量增加而增加，随后又随之下降，但其结晶温度却随ＨＴＨ１０加入而单调下降，共混物的熔融热焓△Ｈｍ在ＨＴＨ１０含量为３０％时与计算值有较大的偏差，广角Ｘ－射线衍射结果表明，此时共混物结构发生了较为明显的变化，两组份之间在此时存在一定的相互作用．The solution-prepared blends of thermotrotropic Liquid crystal copolyester (HTH10) and Nylon-1010 have been investigated by using PLM, DSC and WAXD. It was found that cross polarized micrographs of the blends are as same as the micrographs of HTH10 when the content of HTH10 was over 30%.The crystallinity of Nylon-1010 increased first and then decreased with the increse of HTH10 composition, but the crystallization temperature of Nylon-1010 decreased monotonically. There was a marked derivation of △ Hm from the calculated values when the HTH10 content reached to 30%. The results of wide angle X-ray diffraction on the blends demonstrated that the structure of Nylon-1010 was influenced significantly at the weight rate of 30/70 for the HTH10 and Nylon-1010 blends.

关 键 词：液晶共聚酯 共混物 尼龙1010 PLM LCP 

分 类 号：O633.14[理学—高分子化学] TQ342.14[理学—化学]