K_2NbOF_5－MF_3系玻璃的结构及电性质  

Structure and Electrical Property of K2NbOF_5-MF_3 System Glasses

作　　者：蒋凯[1] 李五聚[1] 杨林[1] 袁启华[1] 

机构地区：[1]河南师范大学化学系,武汉工业大学材料复合新技术国家重点实验室

出　　处：《功能材料》1995年第5期449-452,共4页Journal of Functional Materials

摘　　要：研制了Ｋ＿２ＮｂＯＦ＿５－ＭＦ＿３（Ｍ＝Ａｌ、Ｇａ）新体系氟化物玻璃，测定了玻璃的特征温度、Ｒａｍａｎ光谱和电导率，玻璃中Ｎｂ￣（５＋）、Ａｌ￣（３＋）、Ｇａ￣（５＋）分别以ＮｂＯＦ、ＡＩＦ、ＧａＦ八面体形式存在，玻璃的电导率随ＡｌＦ＿３含量的增加而增加，ＡｌＦ＿３含量达到３０ｍｏｌ％时，Ａｌ￣（３＋）除ＡＩＦ八面体外，还有ＡｌＦ四面体结构出现，同时电导率降低，Ｆ￣－阴离子是主要的导电离子，７５Ｋ＿２ＮｂＯＦ＿５·２５ＡｌＦ＿３玻璃的电导率在１９６℃时，σ＝１．０２×１０￣（－２）Ｓ·ｃｍ￣（－１）。K_2NbOF_5-MF_3(M=Al、Ga)newsystem glasses were prepared.The characteristictempelature,Raman spectra and conductivity ofsome sampes were measured.Nb￣(5+),Al￣(3+)and Ga￣(3+)inthe glasses exist as NbOF,AIF,GaFoctahedrons Conductivity increased with increase ofccntent of AlF_3 When the content of AlF_3 reached30mol%,AIF tetrahedrons turned up besidesAlF octahedrons,and conductivitv decreased.F￣-anion was the chief conducting ion. The conductivityof 75K_2bOF_5·25AlF_3 glass was 1.02×10￣(-2)S·cm￣(-1) at 196℃

关 键 词：氟化物玻璃 快离子导体 玻璃结构 玻璃半导体 