Ni42Cr6Fe封接合金氧化膜和氧化物晶须的结构  

The Structure of Oxide Film and Oxide Whisker on Ni42Cr6Fe Sealing Alloy

作　　者：安白[1] 马莒生[1] 唐祥云[1] 

机构地区：[1]清华大学材料系

出　　处：《功能材料》1995年第5期461-464,共4页Journal of Functional Materials

摘　　要：用ＴＥＭ、Ｘ－Ｒａｙ、ＳＥＭ等技术研究了Ｎｉ４２Ｃｒ６Ｆｅ玻封合金在高温湿Ｈ＿２中形成的氧化膜及氧化物晶须的结构。结果表明：氧化膜主要由Ｃｒ＿２Ｏ＿３和（Ｆｅ，Ｍｎ）Ｃｒ＿２Ｏ＿４两相组成，氧化膜底层是以Ｃｒ＿２Ｏ＿３为主的组织，氧化膜在层是以（Ｆｅ，Ｍｎ）Ｃｒ＿２Ｏ＿４为主的组织；Ｓｉ在氧化膜与合金界面分布，Ａｌ则在内氧化层中形成内氧化物质点；氧化膜表面生长的氧化物晶须的杆部为（Ｆｅ，Ｍｎ）Ｃｒ＿２Ｏ＿４单晶，头部为Ｎｉ＿３Ｆｅ型金属间化合物。The structure of oxide film and oxidewhisker on Ni42Cr6Fe sealing anoy after oxidation inwet hydrogen at high teniperature are st udied usingTEM,X-Ray and SEM methods.The resultsindicate that oxide film is mainly colnposed of Cr_2O_3and(Fe,Mn)Cr_2O_4 spinel。The outer oxide layer iscoarse(Fe,Mn)Cr_2O_4 spinel grains mainly and thebase oxide layer is fine Cr_2O_3 grains mainly.Si-oxideis on the interface of meral and oxide,Al is formed tointernal oxidation in the surface of alloy,The pole ofoxide whisker on the oxide film is the spinel(Fe,Mn )Cr_2O_4 monocrystal,the head of oxide whisker isNi_3Fe

关 键 词：氧化膜 氧化膜晶须 封接合金 气密封接 

分 类 号：TG136[一般工业技术—材料科学与工程]