Microstructure and Strength of Brazed Joints of Ti_(3)Al Base Alloy with Cu-P Filler Metal  

作　　者：Peng HE Jicai FENG Heng ZHOU 

机构地区：[1]National Key Laboratory of Advanced Welding Production Technology, Harbin Institute of Technology, Harbin 15{}001, China

出　　处：《Journal of Materials Science & Technology》2005年第4期493-498,共6页材料科学技术（英文版）

基　　金：This research was financially supported by the National Natural Science Foundation of China(No.50325517).

摘　　要：Brazing of Ti3Al alloys with the filler metal Cu-P was carried out at 1173-1273 K for 60-1800 s. When products are brazed, the optimum brazing parameters are as follows： brazing temperature is 1215-1225 K; brazing time is 250-300 s. Four kinds of reaction products were observed during the brazing of Ti3Al alloys with the filler metal Cu-P, i.e., Ti3Al phase with a small quantity of Cu （Ti3Al（Cu）） formed close to the Ti3Al alloy; the TiCu intermetallic compounds layer and the Cu3P intermetallic compounds layer formed between Ti3Al（Cu） and the filler metal, and a Cu-base solid solution formed with the dispersed Cu3P in the middle of the joint. The interracial structure of brazed Ti3Al alloys joints with the filler metal Cu-P is Ti3Al/Ti3Al（Cu）/TiCu/Cu3P/Cu solid solution （Cu3P）/Cu3P/TiCu/Ti3Al（Cu）/Ti3Al, and this structure will not change with brazing time once it forms. The thickness of TiCu＋Cu3P intermetallic compounds increases with brazing time according to a parabolic law. The activation energy Q and the growth velocity/to of reaction layer TiCu＋Cu3P in the brazed joints of Ti3Al alloys with the filler metal Cu-P are 286 kJ/mol and 0.0821 m2/s, respectively, and growth formula was y2=O.O821exp（-34421.59/T）t.Careful control of the growth for the reaction layer TiCu＋Cu3P can influence the final joint strength. The formation of the intermetallic compounds TiCu＋Cu3P results in embrittlement of the joint and poor joint properties. The Cu-P filler metal is not fit for obtaining a high-quality joint of Ti3Al brazed.Brazing of Ti3Al alloys with the filler metal Cu-P was carried out at 1173-1273 K for 60-1800 s. When products are brazed, the optimum brazing parameters are as follows： brazing temperature is 1215-1225 K; brazing time is 250-300 s. Four kinds of reaction products were observed during the brazing of Ti3Al alloys with the filler metal Cu-P, i.e., Ti3Al phase with a small quantity of Cu （Ti3Al（Cu）） formed close to the Ti3Al alloy; the TiCu intermetallic compounds layer and the Cu3P intermetallic compounds layer formed between Ti3Al（Cu） and the filler metal, and a Cu-base solid solution formed with the dispersed Cu3P in the middle of the joint. The interracial structure of brazed Ti3Al alloys joints with the filler metal Cu-P is Ti3Al/Ti3Al（Cu）/TiCu/Cu3P/Cu solid solution （Cu3P）/Cu3P/TiCu/Ti3Al（Cu）/Ti3Al, and this structure will not change with brazing time once it forms. The thickness of TiCu＋Cu3P intermetallic compounds increases with brazing time according to a parabolic law. The activation energy Q and the growth velocity/to of reaction layer TiCu＋Cu3P in the brazed joints of Ti3Al alloys with the filler metal Cu-P are 286 kJ/mol and 0.0821 m2/s, respectively, and growth formula was y2=O.O821exp（-34421.59/T）t.Careful control of the growth for the reaction layer TiCu＋Cu3P can influence the final joint strength. The formation of the intermetallic compounds TiCu＋Cu3P results in embrittlement of the joint and poor joint properties. The Cu-P filler metal is not fit for obtaining a high-quality joint of Ti3Al brazed.

关 键 词：Brazed joints MICROSTRUCTURE Ti3Al base alloy 

分 类 号：TG146.21[一般工业技术—材料科学与工程]