一种低温烧成的高阿利特硅酸盐水泥熟料的试验研究  

Research of high alite content Portland cement clinker burnt at low temperature

作　　者：张文生[1] 苏林行 叶家元[1] 秦守婉[1] 王宏霞[1] 陈益民[1] 

机构地区：[1]中国建筑材料科学研究院水泥科学与新型建材研究所,北京100024 [2]黑龙江省七台河市发展计划委员会,黑龙江七台河154600

出　　处：《水泥》2005年第8期8-10,共3页Cement

基　　金：国家重点基础研究发展规划(973)项目(2001CB610700)

摘　　要：实验室低温烧制了一种高阿利特硅酸盐水泥熟料并测试了其性能。该熟料中的阿利特含量高于70%,烧成温度≤1400℃。其3d抗压强度可达42.8MPa,28d抗压强度可达65.8MPa。同时这种水泥熟料的易磨性优于普通硅酸盐水泥熟料:在相同条件下,磨细到比表面积320m2/kg时,这种熟料需要4.5min,而普通硅酸盐水泥熟料则需要8.0min。同时对该熟料进行了岩相检验分析。A high alite content Portland cement clinker was burnt at low temperature in laboratory and its performance was tested. The alite content of the clinker exceeded 70%, and the well-burnt temperature below 1400℃, tile 3d and 28 dcompressive strength reach to 42.8MPa and 65.8MPa. The grindability of cement clinker was better than ordinary Portland cement, for example, on the same condition it took the high alite content Portland cement clinker 4.5min to grind to a specific surface area of 320m2/kg, while the ordinary Portland cement needed 8.0min. And further the petrographic study had been implemented

关 键 词：硅酸盐水泥熟料 高阿利特 组成 物理性能 

分 类 号：TQ172.11[化学工程—水泥工业]