纳米Al_2O_3,ZnO,CeO_2,ZrO_2对低温无铅熔块性能的影响  

THE EFFECTS OF NANO-SIZED AlAl_2O_3,ZnO,CeO_2,ZrO_2 ON THE PERFORMANCES OF LOW TEMPERATUER LEAD-fREE FRIT

作　　者：辛崇飞[1] 吴建青[1] 杨金萍[1] 

机构地区：[1]华南理工大学材料学院,广州510640

出　　处：《中国陶瓷》2005年第4期8-11,共4页China Ceramics

基　　金：国家"863"计划资助项目(2002AA302204);广东省科技计划资助项目(2001A1070102);广州市科技计划资助项目

摘　　要：采用正交实验法,研究了在无铅基础熔块中,添加纳米Al2O3,ZnO,CeO2,ZrO2对其抗弯强度、维氏硬度及化学稳定性等性能的影响。结果表明:外加纳米氧化铝等可使无铅熔块抗弯强度提高30%,化学稳定性提高60%～80%,硬度提高10%左右。The effects of nano-sized Al2O3,ZnO,CeO2,ZrO2 on the performances of lead-free frit, such as the flexural strength, HV500 hardness and chemical stability, had been studied using orthogonal method in this paper. The results indicated that the flexural strength was raised by 30%, chemical stability was improved by 60% to 80%,and the HV500 hardness of the samples was raised by 10%,when using Al2O3,ZnO,CeO2,ZrO2 as additives.

关 键 词：无铅熔块 正交实验法 抗弯强度 维氏硬度 化学稳定性 

分 类 号：TQ174.43[化学工程—陶瓷工业]