多壁纳米碳管化学镀钴磷合金  

Electroless Plating of Multiwalled Carbon Nanotubes with Co-P

作　　者：郑重[1] 李四年[1] 陈慧敏[1] 张友寿[1] 余天庆[1] 

机构地区：[1]湖北工业大学材料科学与工程系,430068

出　　处：《新技术新工艺》2005年第8期63-64,共2页New Technology & New Process

基　　金：武汉市晨光计划项目(20015005030);湖北省自然科学基金项目(2002AB49)

摘　　要：碳纳米管经纯化、氧化、敏化、活化预处理后,在碱性镀液中化学镀磁性金属钴磷合金, 得到一维纳米复合材料。探讨了镀覆的最佳工艺参数。利用透射电镜(TEM)及扫描电镜 (SEM)观察施镀前后表层形貌,用能谱分析测试镀层的组成,并用振动磁强检测仪测量了镀 后碳纳米管的磁性能。研究表明,镀后碳纳米管外表面被钴磷合金紧密均匀包覆,矫顽力较之 钴磷膜、钴粉有较大提高,可望在高密度磁记录材料中得到应用。After purification, oxidization, sensitization, and activation pretreatment, the surface of carbon nanotubes was deposited with Co D by the electroless deposition method. The optimum techniques were determined. Before and after plating, the morphology of carbon nanotubes was examined by transmission-electron microscopy （TEM） and scanning electron microscopy （SEM）. Its composition was determined by energy spectrum analysis. And its magnetic properties was gauged. The results demonstrated that the surface of carbon nanotubes is covered by the dip coating of Co-P alloy after plating, and its magnetic coercivity was better than Co film and Co powder which might be useful for high density magnetic recording.

关 键 词：碳纳米管 化学镀 钴 磁性能 

分 类 号：TQ127.2[化学工程—无机化工]