Pyroelectricity and Spontaneous Polarization in [111] Oriented 0.955 Pb（Zn1/3Nb2/3）O3-0.045PbTiO3 Single Crystals  

作　　者：沈明荣 姚东来 曹文武 

机构地区：[1]Department of Physics, Suzhou University, Suzhou 215006 [2]Department of Mathematics and Materials Research Institute, The Pennsylvania State University, University Park, PA 168O2, USA

出　　处：《Chinese Physics Letters》2005年第9期2390-2393,共4页中国物理快报（英文版）

基　　金：Supported by the National Natural Science Foundation of China under Grant No 10204016.

摘　　要：We report that the measurements of the pyroelectric current of the pre-poled [111]-oriented 0.955 Pb（Zn1/3Nb2/3） O3-0.045 PbTiO3 （PZN-4.5%PT） single crystals can shed some light on the phase transition and spontaneous polarization characters of this material in a similar way to measures of remanent polarization and dielectric properties. The pyroelectric current is measured and the corresponding spontaneous polarization is calculated as a function of temperature with various poling fields added during cooling the sample from 200℃ to room temperature. Critical electric field of 0.061 k V/cm is found to be essential to induce the intermediate ferroelectric orthorhombic phase between the ferroelectric rhombohedral and tetragonal phases. Below the critical field, the polarization increases almost linearly with the increase of poling field. At the critical field, the polarization at 30OC increases abruptly from 14μC/cm^2 for a poling field of O.06kV/cm to 29.5μC/cm^2 for a poling field of 0.061 kV/cm, and afterwards, increases slowly and saturates to 31 μC/cm^2 for poling fields beyond 0.55 kV/cm.We report that the measurements of the pyroelectric current of the pre-poled [111]-oriented 0.955 Pb（Zn1/3Nb2/3） O3-0.045 PbTiO3 （PZN-4.5%PT） single crystals can shed some light on the phase transition and spontaneous polarization characters of this material in a similar way to measures of remanent polarization and dielectric properties. The pyroelectric current is measured and the corresponding spontaneous polarization is calculated as a function of temperature with various poling fields added during cooling the sample from 200℃ to room temperature. Critical electric field of 0.061 k V/cm is found to be essential to induce the intermediate ferroelectric orthorhombic phase between the ferroelectric rhombohedral and tetragonal phases. Below the critical field, the polarization increases almost linearly with the increase of poling field. At the critical field, the polarization at 30OC increases abruptly from 14μC/cm^2 for a poling field of O.06kV/cm to 29.5μC/cm^2 for a poling field of 0.061 kV/cm, and afterwards, increases slowly and saturates to 31 μC/cm^2 for poling fields beyond 0.55 kV/cm.

关 键 词：PHASE 

分 类 号：O7[理学—晶体学]