一种亚稳β钛合金的加工图(英文)  

Processing Map of One Kind of Metastable β Titanium Alloy

作　　者：曾立英[1,2] 杨冠军[1] 葛鹏[2] 毛小南[2] 赵永庆[2] 周廉[2] 

机构地区：[1]西安建筑科技大学,陕西西安710055 [2]西北有色金属研究院,陕西西安710016

出　　处：《稀有金属材料与工程》2010年第9期1505-1508,共4页Rare Metal Materials and Engineering

基　　金：International S&T Cooperation Program of China (2006DFA53600);the National Basic Research Program of China (2007CB613805);the National Key Technologies R&D Program (2007BAE07B01)

摘　　要：为了挖掘亚稳β钛合金Ti-B19的热变形加工潜力,采用热模拟试验机,在温度范围750-1000°C,温度间隔50°C,应变速率为0.001-10s-1的条件下对Ti-B19合金的热压缩行为进行研究。结果表明,一定温度下,Ti-B19合金的流变应力随应变速率的增大而增大;一定应变速率下,合金的流变应力则随温度的升高而降低。当应变ε为0.6时,合金的加工图可分为3个区域。700-800°C,应变速率为0.001-0.1s-1,合金最大的能量耗散效率值出现在750°C和0.01s-1处,其数值为42%,出现连续软化之前,此区域的流变曲线中只出现单个峰或振荡峰。第2个区域的温度范围在800-1000°C,应变速率范围为0.001-0.1s-1,能量耗散效率值在29%～36%之间变化。此区域的流变曲线到达稳态之前只出现单个峰或振荡峰,此时可观察到典型的再结晶组织。温度低于800°C,应变速率大于0.1s-1,或者温度高于800°C,应变速率大于10s-1时,合金中会出现典型的流变不稳定的第3区,组织中可观察到绝热剪切带或β相流变不均匀区。In order to exploit the potential hot deformation ability of metastable β titanium alloy Ti-B19 the isothermal compression behavior was investigated by a Gleeble-1500 thermal simulator in the temperature range of 750–1000 °C at an interval of 50 °C and strain rate from 0.001 to 10 s?1. The results indicate that the flow stress of the alloy increases with increasing of the strain rate at a given temperature, and decreases with the increment of temperature at a given strain rate. The processing map for the alloy obtained at strain of 0.6 can be divided into three domains. The first is the one in the temperature range of 700800 °C and the strain rate range of 0.001–0.1 s?1, with a peak efficiency of 42% at about 750 °C and 0.01 s?1. The flow curves in this domain present a single peak or oscillation in the flow curves before continuous softening appears. The second is the one in the temperature range of 800–1000 °C and the strain rate range of 0.001–0.1 s?1, with efficiency from 29% to 36%. The flow curves in this domain present a single peak or oscillation in the flow curves before reaching steady state. Recrystallized structures can be found, which is a typical dynamic recrystallization zone. The third one is a flow instable domain at the temperature lower than 800 °C and the strain rate above 0.1 s?1, or at the temperature higher than 800 °C and strain rate above 10 s?1. The adiabatic shear bands (ASBs) and flow inhomogeneous zone of β phases can be observed.

关 键 词：亚稳Β钛合金 加工图 Kind strain rate 应变速率 FLOW curves range of 温度范围 流变应力 domain 区域 能量耗散 流变曲线 hot deformation processing map 效率值 热模拟试验机 shear BANDS FLOW stress compression 

分 类 号：TG146.23[一般工业技术—材料科学与工程]