PMN基复相弛豫铁电陶瓷电致应变及其温度稳定性的研究  

Electrostrictive Properties and Temperature Stability of Pb(Mg_(1/3)Nb_(2/3))O_3-based Composite Relaxor Ferroelectric Ceramics

作　　者：杨祖培[1] 刘少恒[1] 高峰[2] 田长生[2] 

机构地区：[1]陕西师范大学化学与材料科学学院,西安710062 [2]西北工业大学材料科学与工程学院,西安710072

出　　处：《材料工程》2005年第9期16-18,21,共4页Journal of Materials Engineering

基　　金：陕西省自然科学基金资助项目(2000C03)

摘　　要：用熔盐法制备的不同居里温度的Pb(Mg1/3Nb2/3)O3基陶瓷预烧粉体和烧结粉体为初始高、低温组元,采用混合烧结法制备出PMN基弛豫铁电复相陶瓷,研究了PMN基复相陶瓷的介电性能和电致伸缩性能及其温度稳定性。结果表明:采用烧结粉体制得的复相陶瓷不仅具有较大的介电常数(室温介电常数为8368)和电致应变2.8×10-4,而且在-10^+70℃范围内温度稳定性也较好。The high and low cure temperature Tm component Pb（Mg1/3Nb2/3 ）O3-based ceramic powders were prepared by molten salt synthesis using mixtures of NaCl-KCl salt. The composite ceramics used with PMN-based ferroelectric relaxors were prepared by mixed sintering method. The dielectric, electrostrictive properties and temperature stability were investigated. The results indicate that the ceram- ics not only has excellent dielectric（ε25℃ is 8368 ）and electrostrictive properties （S is 2.8× 10^-4）, but also has better temperature stability from -10℃ to ＋70℃.

关 键 词：PMN基复相陶瓷 介电性能 电致应变 温度稳定性 

分 类 号：TN304.9[电子电信—物理电子学]