陶瓷型芯精铸气冷涡轮叶片气孔分析  

Mechanism of Forming Gas Hole Defect in the Investment Casting for Air Cooled Turbine Blade

作　　者：郑启[1] 唐亚俊[1] 王玉兰[1] 刘一鸣 

机构地区：[1]中国科学院金属研究所 [2]黎明发动机制造公司

出　　处：《特种铸造及有色合金》1996年第3期36-37,共2页Special Casting & Nonferrous Alloys

摘　　要：研究了Ｍ１７Ｆ合金无余量精铸空心气冷叶片气孔形成规律。发现型芯上的积碳是形成大面积蜂窝状气孔的主要原因；合金元素Ｔａ提高了熔融合金的化学活性，是形成气孔的合金因素；型芯中锆英石的分解产物无定形ＳｉＯ２。The mechanism of forming the gas hole defect in the M17F superalloy investment casting for turbine blade was studied. The main affecting factors are that: C left on ceramic core after prefiring shell, Ta, a alloying element, increased the chemical activity of the liquid alloy, and the amorphous SiO 2, a zircon resolvent, helped to bring about the action produced gasses.

关 键 词：高温合金 叶片 气孔 陶瓷型铸造 