碳化钨/高铬铸铁复合铸渗层耐磨特性研究  

Research on Wear-resistance Property of WC/High-Cr Cast Iron Composite Layer

作　　者：陈跃[1] 上官宝[1] 铁喜顺[1] 张永振[1] 贾利晓[1] 李珍[1] 

机构地区：[1]河南科技大学,河南洛阳471003

出　　处：《铸造技术》2005年第10期935-937,共3页Foundry Technology

基　　金：河南省杰出人才创新基金;编号:0421000600;国家自然科学基金重点项目;编号:50432020

摘　　要：采用CO2水玻璃砂型铸渗工艺制备了碳化钨/高铬铸铁复合铸渗层试样,借助于MLD-10动载磨损试验机、扫描电镜研究了渗剂组分、粒度、工艺参数对铸渗层耐磨性的影响,结果表明:在试验条件下,渗剂中加入60～80目的20%碳化钨颗粒、40%高铬铸铁粉获得的铸渗层耐磨性能最佳.复合铸渗层适合于小能量冲击磨损的工况条件.In this paper,samples with WC/high-Cr cast iron composite layer have been gained by CO2 silicatebonder sand mould casting technique,and the influence of alloy component,granularity,process parameter on wear-resistance property of composite layer has been studied by using MLD-10 impact wear experiment machine and SEM. The result showed：The composite layer has the best wear- resistance property when 20% WC and 40% Cr-Fe which all are 60-80 granule are added at the test condition. The composite layer is adapt to status of impact wear with low energy.

关 键 词：铸渗技术 耐磨特性 碳化钨 高铬铸铁 

分 类 号：TG257[金属学及工艺—铸造]