低硅铝锆碳滑板的性能研究  

Properties of low silica Al_2O_3-ZrO_2-C slide plate

作　　者：王瑞生[1] 于之东[2] 杨晓春[3] 卜景龙[1] 

机构地区：[1]河北理工大学材料学院,唐山063009 [2]唐山学院 [3]唐山钢铁公司耐火材料有限公司

出　　处：《耐火材料》2005年第5期341-343,共3页Refractories

基　　金：国家自然科学基金资助项目(50332010)。

摘　　要：针对传统的以锆莫来石为原料的铝锆碳滑板中SiO2含量较多,在浇铸钙处理钢时侵蚀严重的问题,用部分稳定ZrO2(PSZ)代替锆莫来石原料,加入板状刚玉、活性α-Al2O3、炭黑、Si粉、B4C粉和热固性酚醛树脂,分别在1300℃、1400℃、1500℃烧后制成了低硅铝锆碳滑板,并测定了试样的抗渣性、热膨胀系数、膨胀率和热震后强度损失率.结果表明:低硅铝锆碳滑板的烧成温度以1300～1400℃为宜,在此温度下烧成的试样性能优良,其抗热震性和抗渣性均优于以锆莫来石为原料的传统铝锆碳滑板.Using tabular alumina,active α-Al2O3 ,PSZ-ZrO2 and carbon black as main staring materials,the Al2O3-ZrO2-C slide plate with low silica was prepared with Si and B4C as the additives and thermosetting resin as the binder at the temperature of 1300 ℃,1400℃ and 1500℃ separately. The specimens were studied on physical properties, slag resistance ,thermal expansion coefficient,expansion ratio and strength decreasing ratio after thermal shock. The results show that the sintering temperature between 1300℃ and 1400℃ is proper and the low silica Al2O3-ZrO2- C slide plate has excellent thermal shock resistance and slag resistance.

关 键 词：低硅铝锆碳滑板 滑动水口 炼钢工艺 耐火材料 使用性能 

分 类 号：TF065.1[冶金工程—冶金物理化学]