一种近α型钛合金的高温氧化行为  

High-temperture oxidation behavior of one α-Titanium alloy

作　　者：吴玮璐[1] 赵永庆[1] 马雪丹[1] 常辉[1] 郭萍[1] 郭荻子[1] 

机构地区：[1]西北有色金属研究院钛合金所,西安710016

出　　处：《西安工业学院学报》2005年第4期359-361,共3页Journal of Xi'an Institute of Technology

基　　金：国家863计划项目(2002AA336040);国家重点自然基金项目(50434030)

摘　　要：采用扫描电镜、X射线衍射仪等研究了近α型钛合金Ti230在1 000℃～1 300℃特高温氧化行为.研究结果表明,在高于1 000℃的特高温下其氧化动力学曲线呈抛物线-直线规律;在超过氧化产物CuO熔点(1 065℃)氧化时,氧化最外层仅为单一金红石型TiO2,此时氧化层中的CuO挥发,氧化增重有减小的趋势;随氧化温度升高,合金的抗氧化能力降低.Ti230合金经本试验温度氧化所形成的少量液相对Ti230合金的组织形态影响不显著.The oxidation behavior of the a-Titanium alloy Ti230 at temperature range of 1 000℃ to 1 300 ℃ by has been studied SEM, X-ray diffraction. It has been found that the rule of the weigh gain follows the parabolic-linear law. When the oxidation temperature is above over the melting point of CuO （ 1 065℃ ）, the oxidation surface is composed of TiO2, CuO within the oxidation layer volatilizes, and the oxidation weigh gain declines. With the increasing of oxidation temperature, its antioxidant ability decreases.

关 键 词：Ti230合金 特高温氧化 钛合金 