HETEROAROMATIC POLYMERS—HIGH TEMPERATURE POLYPYRROLONES DERIVED FROM 2,6-BIS(3',4'-DIAMINOPHENYL)-4-BIPHENYLPYRIDINE AND VARIOUS AROMATIC DIANHYDRIDES  

作　　者：Hai-xia Yang Jin-gang Liu Xiao-juan Zhao Yan-feng Li Lin Fan Shi-yong Yang 

机构地区：[1]School of Chemistry and Chemical Engineering, Lanzhou University, Lanzhou 730000, China [2]Laboratory of Advanced Polymer Materials, Institute of Chemistry, Chinese Academy of Sciences, Beijing 100080, China

出　　处：《Chinese Journal of Polymer Science》2005年第5期521-529,共9页高分子科学（英文版）

基　　金：This project was supported by the National Natural Science Foundation of China(No.50403025).

摘　　要：A new type of aromatic tetraarnine containing biphenyl moiety in the side chain was synthesized via a modified Chichibabin＇s reaction. 3-Nitro-4-acetamidoacetophenone was reacted with 4-phenyl benzaldehyde in the presence of ammonium acetate to obtain 2,6-bis（3＇,4＇-diaminophenyl）-4-biphenyl pyridine （DPPA）. A series of polypyrrolones （PPys） were prepared using tetraamine and various aromatic dianhydrides via a two-step cyclization procedure. All the PPys show excellent high temperature stabilities with the initial decomposition temperatures of 530-549℃ and residual weight ratio of 49%-80% at 750℃ in nitrogen. The polymers exhibit no apparent glass transition temperatures （Tgs） except PPy-1 （Tg= 327℃）, which is derived from tetraamine DPPA and 2,2-bis[4-（3＇,4＇-dicarboxyphenoxy）-phenyl]propane dianhydride （BPADA）. In addition, the polymers have acceptable mechanical properties with the tensile strength of 65-94 MPa. The PPy films show excellent hydrolysis-resistance in alkaline aqueous medium and could maintain most of the properties even after boiling in 10% aqueous sodium hydroxide solution for a week.A new type of aromatic tetraarnine containing biphenyl moiety in the side chain was synthesized via a modified Chichibabin＇s reaction. 3-Nitro-4-acetamidoacetophenone was reacted with 4-phenyl benzaldehyde in the presence of ammonium acetate to obtain 2,6-bis（3＇,4＇-diaminophenyl）-4-biphenyl pyridine （DPPA）. A series of polypyrrolones （PPys） were prepared using tetraamine and various aromatic dianhydrides via a two-step cyclization procedure. All the PPys show excellent high temperature stabilities with the initial decomposition temperatures of 530-549℃ and residual weight ratio of 49%-80% at 750℃ in nitrogen. The polymers exhibit no apparent glass transition temperatures （Tgs） except PPy-1 （Tg= 327℃）, which is derived from tetraamine DPPA and 2,2-bis[4-（3＇,4＇-dicarboxyphenoxy）-phenyl]propane dianhydride （BPADA）. In addition, the polymers have acceptable mechanical properties with the tensile strength of 65-94 MPa. The PPy films show excellent hydrolysis-resistance in alkaline aqueous medium and could maintain most of the properties even after boiling in 10% aqueous sodium hydroxide solution for a week.

关 键 词：Tetraamine Polypyrrolone PYRIDINE High temperature polymers Film Hydrolysis-resistance. 

分 类 号：O631.3[理学—高分子化学]