EPDM增韧聚丙烯及其脆韧转变机理的研究  

Study on PP toughened by EPDM and the mechsnism of brittle-tough transition

作　　者：李海东[1] 程凤梅[1] 王宇明[1] 白福臣[2] 赵孝伟[3] 

机构地区：[1]长春工业大学化工学院,吉林长春130012 [2]中国科学院长春应用化学研究所,吉林长春130022 [3]中国石油吉化集团公司农药化工有限责任公司,吉林吉林132021

出　　处：《弹性体》2005年第5期23-25,共3页China Elastomerics

基　　金：国家"973"基金资助项目(G1999064800)

摘　　要：聚丙烯/EPDM共混物韧性的测定可以在很宽的温度(25～132 ℃)和组分(EPDM质量分数为0～26%)中进行.发现了增加温度和增加EPDM组分对EPDM增韧的聚丙烯的脆韧转变有相同的影响,发现了聚丙烯/EPDM共混物的脆韧转变温度与EPDM组分之间的相互关系以及聚丙烯/EPDM共混物的拉伸强度和断裂伸长率与EPDM组分之间的相互关系.The toughness of PP/EPDM blends was measured over a wide range of temperature（25-132 ℃ ） and content （0 - 26wt % EPDM）. It was found that incteasing temperature and increasing EPDM content have equivalent effects on the brittle- tough transition of toughening PP with EPDM. Acorrelation was found between the brittle- tough transition tempetature of PP/EPDM blends and EPDM content . It was found that increasing EPDM content, the tensile strength became low. The correlation was found beteen PP/EPDM blends and EPDM content.

关 键 词：聚丙烯/EPDM共混物 冲击强度 拉伸强度 断裂伸长率 脆韧转变 

分 类 号：TQ333.4[化学工程—橡胶工业]