Ni基电阻合金多道次热轧工艺实验模拟  

Simulation on Multipass Hot-Rolling Process of Ni-Based Electric Resisitance Alloy

作　　者：袁晓波[1] 张军良[1] 李中奎[1] 郑欣[1] 张小明[1] 周军[1] 付洁[1] 张廷杰[1] 

机构地区：[1]西北有色金属研究院,陕西西安710016

出　　处：《热加工工艺》2005年第11期41-43,共3页Hot Working Technology

基　　金：国家军工配套研制基金资助项目(k0322)

摘　　要：采用Gleeble-1500热模拟试验机,对Ni-Mo-Cr-Al电阻合金多道次热连轧进行了实验模拟,对变形时的变形抗力进行了测定。通过对变形后试样组织的金相观察,发现当应变速率为1s-1时,该合金组织对应变速率不甚敏感;当应变速率≥10s-1时,边缘组织容易开裂。道次变形量对合金组织及变形抗力影响较大,第四道次(总变形量≥68%)加工过程中,随着加工温度的降低,材料明显硬化。Multipass hot-rolling of Ni-based electric resisitance alloy was simulated on Gleeble-1500 and the deformation resistance was determined during deform process.The deformed specimens were analysised by the observation of optical micrography.The results show that the structure of this alloy is not sensitive to deformation rate at 1 s^-1.The structure of edge is easy to generate cracks when deformation rate is over high （≥10 s^-1）.Deformatinn value of passes has influence on the structure and the deformation resistance of this alloy sharply.During the 4th （total deformation/〉68% ） pass working process,material drive to hardening obviously with the decrease of temperature.

关 键 词：Ni基电阻合金 多道次热轧 热模拟 

分 类 号：TG132.24[一般工业技术—材料科学与工程]