超高碳钢化学成分中铝含量的合理选择  

Rational Al amount in chemical composition of UHCS

作　　者：石淑琴[1] 王宝奇[2] 古原忠[3] 牧正志[3] 

机构地区：[1]天津职业大学机电工程学院,天津300402 [2]河北工业大学材料科学与工程学院,天津300132 [3]京都大学材料工学学科

出　　处：《兵器材料科学与工程》2005年第6期26-30,共5页Ordnance Material Science and Engineering

基　　金：河北省自然科学基金项目(500023)

摘　　要：借助相图计算及试验分析,对含碳1．5％(质量分数)的超高碳钢化学成分铝的合理选择进行了分析研究。结果表 明,随铝含量增加,A1温度升高,珠光体相变组织片层间距减小,网状碳化物减少。随铝含量增加单相奥氏体区变小变无, 液化温度降低,热加工性能恶化。综合考虑,含碳1．5％(质量分数)的超高碳钢化学成分铝的合理添加量应选择为2．0％(质 量分数)左右。By means of the phase diagram calculation and experiment analysis, the rational amount of Al as chemical composition in UHCS was studied. The result indicates that temperature A1 goes up as the Al content increases, while lamellar distance in pearlite phase transformation macrostructure decreases and the network carbide decreases. With Al content increasing, uniphase austenite area decreases or disappears, the liquefaction temperature becomes low, and hot-workability worsens. To sum up, the rational amount of Al to be chosen as about 2.0%（quality fraction） in UHCS with 1.5%（quality fraction） carbon content.

关 键 词：铝元素 超高碳钢 组织相变 热加工性能 

分 类 号：TG113[金属学及工艺—物理冶金] TG142.4[金属学及工艺—金属学]