冷镦钢盘条冷镦开裂原因分析  

Cause Analysis of Crack during Cold Heading of Cold Heading Steel Wire Rod

作　　者：赵自义[1] 雍治文[1] 吴从善[1] 

机构地区：[1]安阳钢铁股份有限公司,455004

出　　处：《金属制品》2005年第5期31-33,共3页Metal Products

摘　　要：盘条中的夹杂、折叠、划伤和晶粒度不均等是造成冷镦钢冷镦开裂的原因.在炼钢时控制钢水的洁净度,连铸时防止钢水卷渣,控制速度为2.4～2.8 m/min,轧钢时采用闭环温度控制、RSM轧制、STELMOR控冷技术.成品尺寸精度达到±0.1 mm,冷镦开裂得到了有效控制.Inclusion, lapping, stamp and uneven grain size are the main cause for crack during cold heading of cold heading steel wire rod. The measures are adopted ： controlling the cleanness of molten steel during steel-making, preventing to roll into residue during continuous casting and controlling the speed of 2.4 - 2.8 m/min, adopting closed loop temperature control, RSM rolling, STELMOR control cooling technique during steel rolling. Dimension precision of finished products is up to ±0.1 mm and crazing during cold heading is controlled in effect.

关 键 词：高速线材 冷镦钢 冷镦开裂 

分 类 号：TG111.91[金属学及工艺—物理冶金]