WCp增强球铁基复合材料模具的制备及其磨损性能  

Producing of WCp Reinforced SG Iron Composites Firebrick Mould And Its Abrasive Wear Behavior

作　　者：李秀兵[1] 刘琛[2] 方亮[1] 

机构地区：[1]西安交通大学材料科学与工程学院,陕西西安710049 [2]陕西理工学院材料科学与工程系,陕西汉中723003

出　　处：《铸造技术》2005年第12期1093-1095,共3页Foundry Technology

摘　　要：针对耐火砖模具的工矿特点,将复合材料设计原理和铸造技术相结合,采用复合剂技术,在普通砂型条件下制备了WCp增强球墨铸铁基表层复合材料模具,并对其三体磨粒磨损性能进行了研究.结果表明,合适的球墨铸铁基体材料的主要成分w为3.7%C、2.1%Si、1.0%Cu和0.3%Mn;铸件表面平整,复合层厚度均匀,可达7～9 mm,复合组织的硬度达到HRC 62以上;复合材料相对于基体材料的耐磨性提高到8以上.Aiming at the working characteristic of the firebrick mould, combining composite design mechanism with foundry technology, using＇ promoter technique＇, a firebrick mould is made by WO particles reinforced spherical graphite （SG） iron matrix composites, The three-body abrasive wear properties of WO particles reinforced SG iron matrix composites were investigated, The results show that the main chemical compositions of matrices recommended are 3. 7% C,2. 1% Si, 1.0% Ou and 0, 3% Mn; the casting has smooth and bright surface, high accuracy dimensional tolerances; the composite layer thickness is distributed very well, its range is 7-9 mm; the hardness of the composites is over HRC62, the relative wear resistance of the composite related to matrix material is increased more than 8 times.

关 键 词：复合剂技术 复合材料 磨损 球铁 

分 类 号：TB331[一般工业技术—材料科学与工程]