Characterization of Ionic Conducting Cross-linked Polyether Electrolytes  

作　　者：陈国荣 

机构地区：[1]Department of Applied Chemistry, Harbin Institute of Technology, Harbin 150001, China

出　　处：《Journal of Wuhan University of Technology(Materials Science)》2005年第4期104-106,共3页武汉理工大学学报（材料科学英文版）

摘　　要：An appropriate amount of toluene 2,4-diisocyanate（TDI） was added into polyether（[（CH2CH2O）13 CH2O]n/Li salt electrolyte to form a cross-linked network,with improving the film proces sability and thermal stability.The relation between the structure and ioinc conductive properties of the cross-lined polyether electrolytes was investigated by means of Fourier transform infra-red spectroscopy（FTIR）,differential scanning calorimetry（DSC）,mechanical property and AC impedance spectroscopy.The electrolytes system is found to have two glass transitions,and it is found that the two Tgs increase with increasing salt concentration.At the some Li salt concentration,the conductivity of cross-liked polyether/LiN（CF3SO2）2 complex system is higher than that of LiClo4,At EO/Li=25：1（mol ratio）,the former conductivity changes with temperature,while the later coincids with Arrhenius formula（σ=Ae^-Ea/RT）.The cross-linked polyether/LiN（CF3 SO2）2 electrolyte exhibits the maximum σ=10^-4.75S/cm at 30℃.An appropriate amount of toluene 2,4-diisocyanate（TDI） was added into polyether（[（CH2CH2O）13 CH2O]n/Li salt electrolyte to form a cross-linked network,with improving the film proces sability and thermal stability.The relation between the structure and ioinc conductive properties of the cross-lined polyether electrolytes was investigated by means of Fourier transform infra-red spectroscopy（FTIR）,differential scanning calorimetry（DSC）,mechanical property and AC impedance spectroscopy.The electrolytes system is found to have two glass transitions,and it is found that the two Tgs increase with increasing salt concentration.At the some Li salt concentration,the conductivity of cross-liked polyether/LiN（CF3SO2）2 complex system is higher than that of LiClo4,At EO/Li=25：1（mol ratio）,the former conductivity changes with temperature,while the later coincids with Arrhenius formula（σ=Ae^-Ea/RT）.The cross-linked polyether/LiN（CF3 SO2）2 electrolyte exhibits the maximum σ=10^-4.75S/cm at 30℃.

关 键 词：CROSS-LINKED polymer electrolyte ionic conductivity two glass transitions 

分 类 号：O631[理学—高分子化学]