Research on Ce-Zr compounds on modifying γ-alumina washcoat on FeCrAl foils  

作　　者：HUANG Ying SHEN Meiqing WANG Jun JIA Liwei 

机构地区：[1]Key Laboratory for Green Chemical Technology of State Education Ministry, School of Chemical Engineering ＆ Technology, Tianjin University,Tianjin 300072, China

出　　处：《Rare Metals》2005年第4期306-312,共7页稀有金属（英文版）

基　　金：[The work was financially supported by the National Key Basic Research Program of China ("973")(No. 2004CB719503).]

摘　　要：Ce-Zr compounds such as Cc0.68Zr0.3202 solid solution, Ce/Zr nitrate and CeO2/ZrO2 were added into γ-alumina-based slurries, which were then loaded on FeCrAl foils pretreated at 950℃ and 1100℃. The microstructures and adhesion performance between the substrates and the washcoats were measured by SEM, BET surface area, ultrasonic vibration and thermal shock test. The results show that the addition of Ce0.68Zr0.32O2 solid solution, Ce/Zr nitrate and CeO2/ZrO2 into the slurries can improve γ-Al2O3-based washcoat adhesion on FeCrAl foils. Furthermore, ceria-zirconia solid solution increases the adhesion of the washcoat on the surface of an FeCrAl foil than the two others. The specific surface area of this washcoat remains about 4345 m^2/g and the weight loss is below 4.0% even after aging test of 10% steam-containing air at 1050℃ for 20 h.Ce-Zr compounds such as Cc0.68Zr0.3202 solid solution, Ce/Zr nitrate and CeO2/ZrO2 were added into γ-alumina-based slurries, which were then loaded on FeCrAl foils pretreated at 950℃ and 1100℃. The microstructures and adhesion performance between the substrates and the washcoats were measured by SEM, BET surface area, ultrasonic vibration and thermal shock test. The results show that the addition of Ce0.68Zr0.32O2 solid solution, Ce/Zr nitrate and CeO2/ZrO2 into the slurries can improve γ-Al2O3-based washcoat adhesion on FeCrAl foils. Furthermore, ceria-zirconia solid solution increases the adhesion of the washcoat on the surface of an FeCrAl foil than the two others. The specific surface area of this washcoat remains about 4345 m^2/g and the weight loss is below 4.0% even after aging test of 10% steam-containing air at 1050℃ for 20 h.

关 键 词：chemical reaction engineering γ-alumina washcoat surface area Ce-Zr compounds metallic substrates 