Electron Concentration Dependence of Transformation Temperature in Different NiMnGa Alloys with First Order Magnetic Transition  

作　　者：Duan Jingfang Zhang Zeyu Wang Dong Long Yi YeRongchang Chang Yongqin 

机构地区：[1]School of Materials Science and Engineering, University of Science and Technology Beijing, Beijing 100083,China

出　　处：《Journal of Rare Earths》2005年第4期I0012-I0012,共1页稀土学报（英文版）

摘　　要：Composition and electron concentration dependence of transformation temperature in Ni2＋x＋y Mn1-xGa1-y, Ni2＋x Mn1-x Ga alloys with first order magnetic transition were studied. For Ni2 ＋ x ＋ y Mn1- x Ga1-y alloys, martensitic transformation temperature TM increases and Curie temperature Tc decreases with the increase of electron concentration e/a, they intercept at e/a = 7.68. TM and Tc decrease when continue to increase electron concentration. While for Ni2＋x Mn1-xGa alloys, they cross at e/a = 7. 635. Before their crossing, the change tendency with e/a is the same as Ni2＋x＋yMn1-xGa1-y alloys;, after their crossing, both TM and Tc increase slowly. The different relations between TM and Tc and e/a within two NiMnGa alloys show that TM and Tc depend not only on e/a, but also on composition.Composition and electron concentration dependence of transformation temperature in Ni2＋x＋y Mn1-xGa1-y, Ni2＋x Mn1-x Ga alloys with first order magnetic transition were studied. For Ni2 ＋ x ＋ y Mn1- x Ga1-y alloys, martensitic transformation temperature TM increases and Curie temperature Tc decreases with the increase of electron concentration e/a, they intercept at e/a = 7.68. TM and Tc decrease when continue to increase electron concentration. While for Ni2＋x Mn1-xGa alloys, they cross at e/a = 7. 635. Before their crossing, the change tendency with e/a is the same as Ni2＋x＋yMn1-xGa1-y alloys;, after their crossing, both TM and Tc increase slowly. The different relations between TM and Tc and e/a within two NiMnGa alloys show that TM and Tc depend not only on e/a, but also on composition.

关 键 词：NiMnGa alloys electron concentration （e/a） martensitic transformation magnetic transition rare earths 

分 类 号：TG146.15[一般工业技术—材料科学与工程]