稠油油溶性降粘剂MASM的合成及室内评价  

Preparation and Laboratory Evaluation of Oil-soluble Viscosity Reducer MASM for Viscous Crude Oil

作　　者：张凤英[1] 李建波[1] 诸林[1] 杨光[2] 

机构地区：[1]西南石油大学化学化工学院,成都610500 [2]西南石油大学油气藏地质与开发工程国家重点实验室,成都610500

出　　处：《精细石油化工进展》2005年第12期5-7,11,共4页Advances in Fine Petrochemicals

摘　　要：以马来酸酐(MA)、甲基丙烯酸甲酯(MMA)、苯乙烯(St)、丙烯酰胺(AM)为原料,甲苯为溶剂,偶氮二异丁腈为引发剂,进行共聚反应,制得MA/MMA/St/AM四元共聚物；再以对甲苯磺酸为催化剂,MA/MMA/St/AM四元共聚物与十八醇进行酯交换反应,制得梳状聚合物,即油溶性降粘剂MASM。确定了共聚反应中最佳合成条件：n(MMA)：n(MA)：n(st)：n(AM)=10：2：3：1,引发剂用量为1.0%,反应温度为70℃。酯交换反应中MA/MMA/St/AM四元共聚物与十八醇最佳摩尔比为1：1。对降粘剂MASM进行了室内评价,结果表明,在50℃下,当降粘剂MASM加量为300mg/L时,降粘率达90.5%。MA/MMA/St/AM tetrapolymer was prepared by copolymeration with maleic anhydride, methyl methacrylate, styrene, and acrylic amide as materials, toluene as solvent, and azodiisobutyronitrile as initiator. The oil - soluble viscosity reducer MASM, a comb - like polymer, was synthesized by transesterification of the tetrapolymer with octadecanol under catalysis of toluene sulfonic acid. The optimum copolymeration condition was as follows： n （MMA）： n（MA） ： n（St） ： n（AM） = 10：2：3：1 ,initiator 1.0% ,reaction temperature 70 ℃ .The optimum molar ratio of MA/ MMA/St/AM tetrapolymer to octadecanol in transesterification was 1 ： 1. The result of laboratory evaluation on viscosity reducer MASM showed that viscosity reduction rate was up to 90.5 % under the condition of temperature 50 ℃ and viscosity reducer MASM 300 mg/L.

关 键 词：降枯剂 稠油 共聚物 油溶性 室内评价 

分 类 号：TE39[石油与天然气工程—油气田开发工程]