Catalytic Activity of Ceria-Zirconia Nanostructured Materials Prepared via Reversed Microemulsion Method  

作　　者：安源 朱凌云 王军 沈美庆 

机构地区：[1]Key Laboratory for Green Chemical Technology of State Education Ministry, School of Chemical Engineering & Technology, Tianjin University, Tianjin 30007, China [2]Key

出　　处：《Journal of Rare Earths》2005年第6期690-694,共5页稀土学报（英文版）

基　　金：ProjectsupportedbytheNational‘973’Project(2004CB719503)

摘　　要：Single-phase homogeneous Ce1-x ZrxO2 solid versed microemulsion method. The structural properties solutions with various compositions were synthesized using the reand performance of Ce1- xZrxO2 were studied using XRD, BET, SEM, HRTEM, TPR and CO oxidation measurements. The results show that in the range of x = 0.4 - 0.5 and x = 0.6 - 1.0, the solid solutions posses the cubic and the tetragonal phase structure, respectively, Solids obtained by the reversed microemulsion method were more homogeneous on the whole range of composition, XRD investigations of the prepared materials did not show segregation of cerium or zirconium oxides, Highly uniform nanosize solid solution particles of ceria-zirconia with high specific area （146.7 m^2·g^-1） were attained under the conditions of this study. The TPR results and CO oxidation measurements indicate that the performance of the CeO2-ZrO2 mixed oxides is strongly related to the composition and structure of the oxides. Enhancement of the activity was found for the catalyst prepared by reversed microemulsion method as compared to the sample prepared by sol-gel method.Single-phase homogeneous Ce1-x ZrxO2 solid versed microemulsion method. The structural properties solutions with various compositions were synthesized using the reand performance of Ce1- xZrxO2 were studied using XRD, BET, SEM, HRTEM, TPR and CO oxidation measurements. The results show that in the range of x = 0.4 - 0.5 and x = 0.6 - 1.0, the solid solutions posses the cubic and the tetragonal phase structure, respectively, Solids obtained by the reversed microemulsion method were more homogeneous on the whole range of composition, XRD investigations of the prepared materials did not show segregation of cerium or zirconium oxides, Highly uniform nanosize solid solution particles of ceria-zirconia with high specific area （146.7 m^2·g^-1） were attained under the conditions of this study. The TPR results and CO oxidation measurements indicate that the performance of the CeO2-ZrO2 mixed oxides is strongly related to the composition and structure of the oxides. Enhancement of the activity was found for the catalyst prepared by reversed microemulsion method as compared to the sample prepared by sol-gel method.

关 键 词：CeO2-ZrO2 solid solution reversed microemulsion NANOSIZE catalytic property carbon monoxide oxidation rare earths 

分 类 号：O643.36[理学—物理化学]