Growth and Spectral Properties of Nd^(3+) Doped KLa(MoO_4)_2 Crystal  

作　　者：WANG Guo-Jian HAN Xiu-Mei LONG Xi-Fa WANG Guo-Fu 

机构地区：[1]Fujian Institute of Research on the Structure of Matter, The Chinese Academy of Sciences, Fuzhou, Fujian 350002, China [2]Graduate School of the Chinese Academy of Sciences, Beijing 100039, China

出　　处：《Chinese Journal of Structural Chemistry》2006年第2期192-196,共5页结构化学（英文）

基　　金：This work was supported by the National Natural Science Foundation of China (50272066) and Key Project of Science and Technology of Fujian (2001H107)

摘　　要：Nd^3＋ doped KLa（MoO4）2 single crystal with the size up to Ф25 × 40 mm^3 was grown by the Czochralski technique. The absorption and luminescence spectra of trivalent neodymium in KLa（MoO4）2 crystal were investigated at room temperature. The absorption and emission cross 10-20 sections are 3.02 ×10^-20 cm^2 at 808 nm and 20.01 × 10^-2 cm^2 at 1061 nm, respectively. The fluorescence lifetime is 164μs at room temperature.Nd^3＋ doped KLa（MoO4）2 single crystal with the size up to Ф25 × 40 mm^3 was grown by the Czochralski technique. The absorption and luminescence spectra of trivalent neodymium in KLa（MoO4）2 crystal were investigated at room temperature. The absorption and emission cross 10-20 sections are 3.02 ×10^-20 cm^2 at 808 nm and 20.01 × 10^-2 cm^2 at 1061 nm, respectively. The fluorescence lifetime is 164μs at room temperature.

关 键 词：Nd^3＋ ：KLa（MoO4）2 crystal crystal growth spectral properties 

分 类 号：O74[理学—晶体学] O78