新型絮凝剂含硼聚硅酸硫酸铁锌的制备及性能研究  

Studies on Property and Prepartion of Polysilicic Acid-ferric and Zinc Sulfate Containing Boron

作　　者：杜杰[1] 张诚[1] 王婷[1] 丁珂[1] 

机构地区：[1]西北工业大学理学院应用化学系,陕西西安710072

出　　处：《上海化工》2006年第2期18-21,共4页Shanghai Chemical Industry

摘　　要：制备了含硼聚硅酸硫酸铁锌絮凝剂(PSFZB),通过正交试验确定最佳制备工艺条件:硅酸聚合时间50分钟、Si/Fe为1∶0.5、Si/Zn为1∶4、B/Si为0.8;研究了其絮凝性能。同时利用X光衍射分析方法、微电泳技术对PSFZB的形态和絮凝机理进行讨论。试验结果表明,研制的PSFZB絮凝剂具有很好的稳定性和较佳的处理效果,是一种较PAC、PFC优良的絮凝剂。The flocculant polysilicic acid-ferric and zinc sulfate containing boron was prepared. The optimum technological conditions are got by experiments.the polymerization time of polysilicic acid 50 min Si/Fe 1：0.5,Si/Zn 1：4,B/Si 0.8. The pattern and flocculent mechanism of PSFZB were studied by using XRD instrument analysis method and electrophoretic mobility measurement. The results show that the PSFZB is a flocculant with good stability and good effect.It is much better than the PAC and PFS.

关 键 词：无机絮凝剂 制备 性能 

分 类 号：TQ317[化学工程—高聚物工业]