CoFe_2O_4铁氧体纳米颗粒的结构与磁性  

Microstructure and Magnetic Properties of Nanosized CoFe_2O_4 Particles

作　　者：王丽[1] 周庆国[1] 孙建荣[1] 王海波[1] 李发伸[1] 

机构地区：[1]兰州大学教育部磁学与磁性材料重点实验室,甘肃兰州730000

出　　处：《磁性材料及器件》2006年第1期23-25,共3页Journal of Magnetic Materials and Devices

摘　　要：用聚乙烯醇（PVA）溶胶-凝胶法制备出CoFe2O4纳米微粉，用X射线衍射（XRD）研究了C0铁氧体纳米颗粒的结构，用振动样品磁强计（VSM）测量了宏观磁性随焙烧温度的变化。随焙烧温度的升高，矫顽力下降，而饱和磁化强度升高。323～873K的变温穆斯堡尔谱测量发现纳米颗粒的磁转变温度Tc在793～813K之间，比块体材料的磁转变温度要低。CoFe2O4 ferrite nanoparticles were prepared by PVA sol-gel method. The crystalline structure was investigated by X-ray diffraction （XRD）. Magnetization measurements were carried out by vibrating sample magnetometer（VSM） at room temperature. With increasing annealing temperature, the coereivity Hc decreases and the saturation magnetization Ms increases. Moessbauer spectra at temperature from 323 to 873K show that the Tc of nanosized CoFe2O4 is at a temperature range of 793 to 813K, which is much lower than that of the bulk counterparts.