1,3-2,4-二亚(对乙基)苄基山梨醇的合成  

Synthesis of 1,3-2,4-di(p-ethyl)benzylidene sorbitol

作　　者：于涛[1] 曲广淼[1] 丁伟[1] 

机构地区：[1]大庆石油学院,黑龙江大庆163318

出　　处：《化工科技》2006年第1期21-23,共3页Science & Technology in Chemical Industry

基　　金：黑龙江省教育厅资助项目(10541013)

摘　　要：以对乙基苯甲醛和山梨醇为原料,对甲苯磺酸为催化剂,在混合溶剂中合成出1,3-2,4-二亚(对乙基)苄基山梨醇透明成核剂,通过正交实验确定了最佳合成工艺条件,反应物料为n(对乙基苯甲醛)∶n(山梨醇)=2.2∶1,混合溶剂为V(环己烷)∶V(甲醇)=2∶1,催化剂用量为山梨醇质量的1.5%,在此工艺条件下,产物收率95%以上。测定了产物的熔点和红外光谱。1,3 2,4-Di （p-ethyl） benzylidene sorbitol nucleating agent was synthesized from p-ethyl benzaldehyde and sorbitol with p-toluene sulfonie acid as catalyst in mixture solvent. The optimum reaction conditions determined by orthogonal experiments were that the nlolar ratio of p-ethyl benzaldehyde to sorbitol was 2.2, the volume ratio of cyclohexane to methanol was 2.0 ,and the amount of catalyst was 1.5%. At these conditions,the yield of the product was over 95%. The melting temperature and IR spectrum of the product were measured.

关 键 词：1 3-2 4-二亚(对乙基)苄基山梨醇 成核剂 合成 