陈化方式对正辛醇改性负载钛催化剂合成聚丁二烯的影响  

The effect of aging condition on polymerization of butadiene with supported titanium catalyst modified by n-octanol

作　　者：高榕[1] 于涛[1] 姚薇[1] 赵永仙[1] 黄宝琛[1] 

机构地区：[1]青岛科技大学橡塑材料与工程教育部重点实验室,山东青岛266042

出　　处：《弹性体》2006年第1期5-7,共3页China Elastomerics

基　　金：国家"863"计划新材料领域"九五"资助项目(863-715-007-0040)

摘　　要：采用n(正辛醇)/n(Ti)=30改性TiCl4/MgCl2合成中乙烯基聚丁二烯弹性体,考察了陈化方式及条件对单体转化率和聚合物相对分子质量的影响。结果表明:Bd-Al-Ti三元陈化催化剂聚合活性高于Al-Ti二元陈化;最佳陈化条件:陈化单体n(Bd)/n(Ti)=20,陈化温度60℃,陈化时间30min;60℃三元陈化所得产物的相对分子质量高于室温(20℃)三元陈化的;而二元陈化产物的相对分子质量高于三元陈化,且随陈化时间的延长,聚合物的特性粘数先上升后下降。The medium vinyl polybutadiene elastomer was synthesized with TiCl4/MgCl2 modified by n-octanol with n （n-octanol）/n （Ti） ratio of 30. The effect of aging condition on conversion and relative molecular weight was investigated. The results showed that the polymerization activity of modified catalyst with the Bd-AI-Ti triad aging mode was higher than that with the Al-Ti-dimerous aging mode. The optimum aging condition was n （Bd）/n （Ti） = 20 ; 30 min; 60 ℃ . In the case of triad aging mode, the relative molecular weight of polybutadiene was higher when catalyst aged at 60 ℃ than that at room temperature （20 ℃ ）. Furthermore,the relative molecular weight of polybutadiene with the Al-Ti dimerous aging mode was higher than that with the Bd-Al-Ti triad mode The intrinsic viscosity of polybutadiene increased and then decreased with the aging time increasing.

关 键 词：正辛醇 负栽钛催化剂 聚丁二烯 陈化 

分 类 号：TQ333.2[化学工程—橡胶工业]