Solidification microstructures in a short fiber reinforced alloy composite containing different fiber fractions  

作　　者：JING Qing-xiu ZHU Ying-lu 

机构地区：[1]School of Material and Chemical Engineering, Jiangxi University of Science and Technology, Ganzhou, 341000,P. R. China

出　　处：《China Foundry》2006年第1期26-29,共4页中国铸造（英文版）

基　　金：The project was financially supported by the Ministry of National Education (No.00191) and the Natural ScienceFoundation of Jiangxi Province (No.0150032)

摘　　要：The solidification microstructures and micro-segregation of a fiber reinforced Al-9 Cu alloy, containing different volume fractions of Al2O3 short fibers about 6μm diameter and made by squeeze casting have been studied. The results indicate that as volume fraction of fiber Vf. increases, the size of final grains becomes finer in the matrix. If λf 〉λ〉1, the fibers have almost no influence on the solidification behavior of the matrix, so the final grains grow coarse, where λf is the average inter-fiber spacing and A is the secondary dendrite arm spacing. While if λf/ 〈λ〈1, the growth of crystals in the matrix is affected significantly by the fibers and the grain size is reduced to the value of the inter-fiber spacing. The fibers influence the average length of a solidification volume element L of the matrix and also influence the solidification time 8, of the matrix. As a result of fibers influencing L and θl, the micro-segregation in the matrix is improved when the composite contains more fibers, although the level of the improvement is slight. The Clyne-Kurz model can be used to semi-quantitatively analyze the relationship between Vf and the volume fraction .fe of the micro-segregation eutectic structure.The solidification microstructures and micro-segregation of a fiber reinforced Al-9 Cu alloy, containing different volume fractions of Al2O3 short fibers about 6 μm diameter and made by squeeze casting have been studied. The results indicate that as volume fraction of fiber Vf increases, the size of final grains becomes finer in the matrix. If λf /λ>1, the fibers have almost no influence on the solidification behavior of the matrix, so the final grains grow coarse, where λf is the average inter-fiber spacing and λ is the secondary dendrite arm spacing. While if λf /λ<1, the growth of crystals in the matrix is affected significantly by the fibers and the grain size is reduced to the value of the inter-fiber spacing. The fibers influence the average length of a solidification volume element L of the matrix and also influence the solidification time θt of the matrix. As a result of fibers influencing L and θt, the micro-segregation in the matrix is improved when the composite contains more fibers, although the level of the improvement is slight. The Clyne-Kurz model can be used to semi-quantitatively analyze the relationship between Vf and the volume fraction fe of the micro-segregation eutectic structure.

关 键 词：short fiber COMPOSITE fiber fractions volume fraction MICRO-SEGREGATION 

分 类 号：TG[金属学及工艺]