钢渣预处理含铬废水及其废渣与铬渣的固化  

Pretreatment of chromium-containing wastewater with steel slag and solidification of waste steel slag and chromium residue

作　　者：宁丰收[1] 游霞[1] 杨海林[1] 谢海富[1] 

机构地区：[1]重庆工商大学环境与生物工程学院,重庆400067

出　　处：《环境污染治理技术与设备》2006年第4期120-123,131,共5页Techniques and Equipment for Environmental Pollution Control

摘　　要：用钢渣对含铬废水进行预处理,探讨了钢渣粒度、用量、废水pH值和添加硫酸亚铁还原剂的影响。结果表明,经硫酸亚铁还原处理后再用钢渣处理比单纯用钢渣处理的效果明显提高,采用钢渣/总铬质量比为40的100目钢渣处理经硫酸亚铁还原后的含铬废水,总铬和Cr6+去除率分别达79%和84%,采用钢渣柱进行的两级淋滤实验进一步表明该方法可作为工业上含铬废水处理的预处理段。处理后的废钢渣同工业铬渣一起进行水泥固化,标准养护20 d后固化体表面Cr6+浸出率、破碎至5 mm粒径以下和酸雨淋溶下的浸出液Cr6+浓度均符合安全标准,可作为普通建材或进行填埋处置。Chromium-containing wastewater was pretreated with steel slag. The influences of granularity and dosage of steel slag, pH value of wastewater, additive ratio of reducer FeSO4 on the treatment efficiency were discussed. The results showed that the effect of the treatment after adding reducer FeSO4 is evidently improved. The removal rates of total chromium and Cr^6＋ came up to 79% and 84% under the conditions of the mass ratio 40 of steel slag to total chromium. The eluviation experiment of the two-stages column filled with steel slag farther showed this process can be used as the pretreatment stage of chromium-containing wastewater treatment in industry. Treated waste steel slag and industrial chromium residue were solidified by cement. After 20 days of standard curing, solidified body can be used as ordinary structural material or can be filled. Superficial Cr^6＋ leaching rate of solidified body, leaching Cr^6＋ consistency of grain broke up under diameter 5 mm and simulant acid rain eluviation satisfied the safe standards.

关 键 词：含铬废水 钢渣 水处理 固化 铬渣 

分 类 号：X703.1[环境科学与工程—环境工程]