聚丙烯酰胺改性水泥砂浆的强度与工艺研究  

Study on Technology and Strength of Polyacryamide Modified Cement Mortar

作　　者：孙增智[1] 申爱琴[1] 胡长顺[1] 

机构地区：[1]长安大学特殊地区公路工程教育部重点实验室,陕西西安710064

出　　处：《公路交通科技》2006年第4期33-36,共4页Journal of Highway and Transportation Research and Development

基　　金：西部交通科技资助项目(2002ZB06)

摘　　要：通过抗压强度试验、抗折强度试验、凝结时间试验与水泥净浆和水泥砂浆的搅拌工艺试验,研究了聚丙烯酰胺改性水泥净浆和水泥砂浆的性能及改性机理。研究结果表明:聚丙烯酰胺对水泥砂浆的搅拌工艺和凝结时间有显著影响,而且对提高水泥砂浆的抗折强度与抗压强度有显著作用,并可降低压折比。Through compressive strength test, flexural strength test, cement setting time test, and mixed technology, test of cement slurry and cement mortar. The modifying effect of mechanism and property of polyaeryamide modifying cement slurry and cement mortar are studied.Relevant test and analysis show that polyacryamide can obviously affect mixing technology, and setting time of cement slurry.Moreover, polyacryamide can not only effectively enhance flexural strength and compressive strength, but also decrease the ratio of compressive strength to flexural strength.

关 键 词：聚丙烯酰胺 凝结时间 抗折强度 抗压强度 压折比 