高炉煤气管系用金属波纹管膨胀节失效机理分析及对策  

Analysis and Countermeasure of Failure Mechanism of Metallic Bellows Expansion Joint in Piping Line of Blast Furnace Gas

作　　者：高志平[1] 周雁[1] 孟宪春 魏守亮 

机构地区：[1]秦皇岛首秦金属材料有限公司,河北秦皇岛066003 [2]秦皇岛北方管业有限公司,河北秦皇岛066004

出　　处：《压力容器》2006年第4期47-50,共4页Pressure Vessel Technology

摘　　要：从首秦金属材料有限公司1200 m3高炉煤气管系波纹管膨胀节多次发生破裂泄漏的情况入手,对其失效机理进行了分析研究,其原因是由于受到高炉煤气中强酸性介质影响,造成316L波纹管膨胀节出现应力腐蚀。并针对这种情况进行分析研究和相关材料试验后,采取更换膨胀节的波纹管材质为Incoloy800来解决此问题,保证了高炉煤气管系的稳定运行。This paper starts with the case of several cracks and leakages of bellows expansion joint in the piping line of 1200 m^3 blast furnace gas in Shouqin Metal Material Co., Ltd., and has a detailed analysis and research on its failure mechanism. Affected by the super acidic media in blast furnace gas, the SUS316L bellows expansion joint appeared stress corrosion. After the analysis and research as well as the related material test according to this case, the material Incoloy800 of bellows expansion joint was used to replace the old material in order to solve the problem. As a result, it assured that blas furnace gas piping line worked steadily.

关 键 词：高炉煤气管系 波纹管膨胀节 应力腐蚀 机理分析 

分 类 号：TQ050.7[化学工程]