w_V/w_C对Cr-Mo-V精铸热锻模具钢高温磨损性能的影响  

Effects of w_V/w_C on High Temperature Wear of Cr-Mo-V Cast Hot-Forging Die Steel

作　　者：王树奇[1] 陈康敏[1] 崔向红[2] 洪扁[1] 

机构地区：[1]江苏大学材料科学与工程学院,江苏镇江212013 [2]吉林大学材料科学与工程学院,吉林长春130022

出　　处：《金属热处理》2006年第4期15-18,共4页Heat Treatment of Metals

基　　金：国家计委产业化前期关键技术与成套设备研制开发项目(1999317)

摘　　要：研究了不同wv／wc对Cr-Mo-V精铸热锻模具钢的高温磨损性能的影响，并探讨了其磨损机理。结果表明，当wv／wc为1．5（0．3／0．2）-2．5（0．5／0．2）时，精铸热锻模具钢磨损率高，耐磨性差；wv／wc为3（1．2／0．4）时，磨损率最低。精铸热锻模具钢高温磨损机理为氧化物疲劳剥落，磨面上产生的氧化物为Fe3O4和Fe2O3，对磨损起到保护作用。The effects of wv/wc on high-temperature wear property of Cr-Mo-V cast hot-forging die steel were studied. The mechanism of high-temperature wear was discussed. The results show that the cast steels with a wv/wc of 1.5 （0. 3/ 0. 2 ） - 2. 5 （0. 5/0. 2 ） have the low wear resistance with higher wear rate ; when wv/wc is 3 （ 1.2/0. 4）, wear rate reaches the lowest. The oxides produced on worn surface are Fe3O4 and Fe2O3 , which have a protection function from wear. The high temperature wear mechanism of the steel is oxide fatigue exfoliation.

关 键 词：热锻模具 铸钢 高温磨损 wv/wc 

分 类 号：TG142.45[一般工业技术—材料科学与工程] TG162.4[金属学及工艺—金属材料]