固液混合铸造Al-40%Cu合金的微观组织  

Microstructure of Al-40%Cu Alloys by Mixed Solid-Liquid Casting

作　　者：黄雅妮[1] 高文理[1] 陈葵[1] 何建军[1] 吴有伍[1] 陈振华[1] 

机构地区：[1]湖南大学材料科学与工程学院,湖南长沙410082

出　　处：《铸造》2006年第5期460-462,共3页Foundry

基　　金：国家自然科学基金资助项目(50274037)

摘　　要：利用固液混合铸造制备了Al-40%Cu合金并对合金的微观组织进行了研究。结果表明:固液混合铸造Al-40%Cu合金中的初生CuAl2多为粒状,尺寸一般为30～80μm。固液混合铸造加入的合金粉能够对Al-40%Cu合金凝固过程产生影响,从而细化合金中初生CuAl2,改善合金组织。与普通铸造和半固态铸造的相比,固液混合铸造Al-40%Cu合金中的初生CuAl2尺寸明显减小,形貌特征得到明显改善。The microstructure of Al-40% Cu alloys produced by the mixed solid-liquid casting was investigated by OM and SEM. The results show that the primary CuAl2 in Al-10%Cu alloys are almost granule and their size is about 30-80 μm. The powder of Al-20%Cu alloys that was added during the process plays an important role in the solidification of Al-40%Cu alloys, and then the primary CuAl2 are finer, so the microstructure of Al-40% Cu alloy is improved. The primary CuAl2 of Al-40% Cu alloy obtained by the mixed solid-liquid casting is smaller in size and its morphology is better than that prepared by conventional casting and semi-solid casting.

关 键 词：铸造 固液混合铸造 AL-CU合金 组织 

分 类 号：TG27[金属学及工艺—铸造]