8^#新锆合金的组织与耐蚀性能的研究  

Study on Structure and Corrosion Resistance of 8 #New Zirconium Alloy

作　　者：朱梅生[1] 刘建章[1] 李中奎[1] 宋启忠[1] 

机构地区：[1]西北有色金属研究院

出　　处：《稀有金属材料与工程》1996年第4期34-38,共5页Rare Metal Materials and Engineering

摘　　要：研究了８＃新锆合金的组织与耐蚀性能。在高压釜中进行了３６０，４００℃和５００℃的腐蚀试验。腐蚀结果表明，８＃合金的抗均匀腐蚀性能和抗疖状腐蚀性能均优于Ｚｒ－４合金。在４００℃、１０．３ＭＰａ水蒸汽中腐蚀１６８天时，８＃合金的增重为Ｚｒ－４合金的８０％左右。５００℃腐蚀２００ｈ后，８＃合金仍未出现疖状腐蚀。ＴＥＭ观察表明，α－Ｚｒ晶内及晶界上存在着许多Ｚｒ（ＦｅＣｒ）２的第二相粒子。The structure and corrosion resistance of 8 #new zirconium alloy are studied. The corrosion tests a the temperatures of 360℃, 400℃ and 500℃ have been carried out in autoclaves. The corrosion results show that 8 #alloy is better than zircaloy-4 for both uniform corrosion resistance and nodular corrosion resistance. When exposured in steam at 400℃, 10.3 MPa for 168 days, the weight gain of 8 #alloy is about 80% of that of zircaloy-4. After 8 #alloy was exposed for 200 hours at 500℃,the nodules have never been observed on the surface of the alloy. TEM observation shows that many second phase particles of Zr(Fe, Cr) 2 whih haxagonal structure exist in the grains and on the grain boundary ofα-Zr.

关 键 词：耐蚀性 锆合金 组织 腐蚀 

分 类 号：TG146.414[一般工业技术—材料科学与工程]