二元胺交联合成高吸水性树脂及其性能研究  

SYNTHESIS AND PERFORMANCE STUDY OF DUALITY SUPERABSORBENT

作　　者：高琼芝[1] 王正辉[1] 

机构地区：[1]华南农业大学理学院应用化学系,广东广州510642

出　　处：《高分子材料科学与工程》2006年第3期70-72,共3页Polymer Materials Science & Engineering

基　　金：广东省自然科学基金资助项目(30506);华南农业大学校长基金资助项目(2004X017)

摘　　要：以过硫酸钾为引发剂,水为分散介质,丙烯酸钠和甲基丙烯酸缩水甘油酯(GM A)共聚得共聚物P(AAN a-GM A),然后利用乙二胺(EDA)使氧杂环开环发生交联反应,制得高吸水性树脂。其结构经1H-NM R和IR表征。用茶袋法研究了乙二胺用量对树脂吸水能力的影响。结果表明,当n(EDA)/n(GM A)=0.35时,得到的树脂的吸水能力最大,达到527倍。Poly （Acrylic acid- Glycidyl methacrylate） s[P （AA-GMA） s]were synthesized by means of copolymerization of acrylic acid and glycidyl methacrylate with potassium peroxydisul-fate as an initiator and water as dispersed phase. With the reaction between crosslinking agent ethylene diamine（EDA） and oxygen heterocycles of P（AA-GMA）, superabsorbent were formed. The polymer P（AA-GMA）was characterized by IR and ^1H-NMR. The relationship between molar ratio n（EDA）/n（GMA） and absorbability was studied by tea-bag method. The results show that the maximum absorbability of superabsorbent reaches 527 times when n（EDA）/n（GMA）= 0.35.

关 键 词：高吸水性树脂 共聚 后交联 

分 类 号：TB34[一般工业技术—材料科学与工程]