Effect of graphite flake addition on the curing procedure of epoxy adhesives

作　　者：郑小玲[1] 杨德容[1] 游敏[1] 张晶晶[1] 

机构地区：[1]三峡大学机械与材料学院,宜昌443002

出　　处：《现代制造工程》2006年第5期80-81,107,共3页Modern Manufacturing Engineering

基　　金：湖北省教育厅科研计划重大项目(2003Z001)

摘　　要：用应变片电测法和阿基米德法,分别测定了鳞片石墨含量不同的环氧胶加热固化中的应变和固化完成后试样的密度,以研究石墨含量对金属-环氧胶接头胶层固化内应力的影响。结果表明:在所采取的研究条件下,石墨含量为5%的试样固化收缩应变值最大,而最初9m in所测得的应变谷值与试样峰值应变和最终应变之差,对应石墨鳞片含量存在着较为一致的对应关系。对鳞片石墨含量变化所带来的影响进行了讨论,综合考虑多方面因素,石墨鳞片的添加量为15%较为适宜。By means of the strain gauges method and Archimedes＇ principle, the influence of graphite flake addition on the density and the inner stress formed in curing procedure were investigated through the strain measured during heating curing as well as the weight and volume of cured specimen. The results obtained shown that the minimum value of density is obtained with 5 % graphite flake added in while the curing contraction strain also reached its maximum value. It is founded that the valley value at first stage curing is corresponding to the contraction strain value during curing. The influence of the variety of graphite flake on the shear strength and curing procedure is also discussed. It is suitable for 15% graphite flake added to the epoxy adhesives when the factors are taken account for.

关 键 词：环氧胶层 鳞片石墨 固化 应变片 

分 类 号：TQ630.1[化学工程—精细化工]