八异戊氧基酞菁铅旋涂膜对NO_2的气敏性研究  

The Study of Gas Sensing Properties of Octa-Iso-Pentyloxymetallophthalocyanine Lead Spin-Coated Films to NO_2

作　　者：李赞[1] 左霞[1] 王彬[1] 陈志敏[1] 吴谊群[1] 

机构地区：[1]黑龙江大学化学化工与材料学院功能材料实验室,哈尔滨150080

出　　处：《传感技术学报》2006年第3期555-558,共4页Chinese Journal of Sensors and Actuators

基　　金：黑龙江省教育厅资助(10551239;10541170)

摘　　要：为了筛选性能优良的酞菁类气敏性材料,设计合成了可溶性的八异戊氧基酞菁铅。利用旋涂技术制备了较理想的八异戊氧基酞菁铅旋涂膜,研究了八异戊氧基酞菁铅旋涂膜对NO2气体的敏感特性。研究表明,室温下八异戊氧基酞菁铅旋涂膜对NO2表现出良好的敏感性,响应浓度为5mg·m-3,响应恢复较快,对浓度为40mg·m-3的响应时间为30s,恢复时间为1.5min,并且该旋涂膜对NO2气体表现出较理想的可逆性、稳定性和选择性。Octa-iso-pentyloxyphthalocyanine lead with high solubility was designed and synthesized to choose good characteristic phthalocyanine gas sensing material. The ideal spin-coated film of PbPc（isoPeO）8 was fabricated by spin-coating technique. The gas sensitivities and mechanism of spin-coated film of PbPc（iso-PeO）8 to NOz were studied. The result showed that the spin-coated film of PbPc（iso-PeO）8 had good sensitivity to NOz at room temperature, could examine 5 mg·m^-3 concentration of NOz. The response time to NOz with 40 mg·m^-3 was 30 s, recovery time was 1.5 min, and the spin-coated films to NOz showed ideal reversibility, stability and selectivity.

关 键 词：异戊氧基酞菁铅 旋涂膜 气敏特性 响应恢复时间 

分 类 号：O647.1[理学—物理化学]