Structure Character of M-A Constituent in CGHAZ of New Ultra-Low Carbon Bainitic Steel under Laser Welding Conditions  

作　　者：Lin ZHAO Wuzhu CHEN Wudong ZHANG Jiguo SHAN 

机构地区：[1]Department of Mechanical Engineering, Tsinghua University, Beijing 100084, China [2]Key Laboratory for Advanced Materials Processing Technology, Ministry of Education, Tsinghua University, Beijing 100084, China

出　　处：《Journal of Materials Science & Technology》2006年第3期382-386,共5页材料科学技术（英文版）

摘　　要：800 MPa grade new ultra-low carbon bainitic （NULCB） steel is the recently developed new generation steel. The microstructure in the coarse-grained heat affected zone （CGHAZ） of NULCB steel under laser welding conditions was investigated by thermal simulation. The influence of the cooling time from 800℃ to 500℃.t8/5 （0.3-30 s）, on the microstructure of the CGHAZ was discussed. The experimental results indicate that the microstructnre of the CGHAZ is only the granular bainite which consists of bainitic ferrite （BF） lath and M-A constituent while t8/5 is 0.3-30 s. The M-A constituent consists of twinned martensite and residual austenite, and the change of the volume fraction of the residual austenite in the M-A constituent is very small when t8/5 is between 0.3 and 30 s. The morphology of the M-A constituent obviously changes with the variation of t8/5.As t8/5 increases, tile average width, gross and shape parameter of the M-A constituent increase, while the line density of the M-A constituent decreases.800 MPa grade new ultra-low carbon bainitic （NULCB） steel is the recently developed new generation steel. The microstructure in the coarse-grained heat affected zone （CGHAZ） of NULCB steel under laser welding conditions was investigated by thermal simulation. The influence of the cooling time from 800℃ to 500℃.t8/5 （0.3-30 s）, on the microstructure of the CGHAZ was discussed. The experimental results indicate that the microstructnre of the CGHAZ is only the granular bainite which consists of bainitic ferrite （BF） lath and M-A constituent while t8/5 is 0.3-30 s. The M-A constituent consists of twinned martensite and residual austenite, and the change of the volume fraction of the residual austenite in the M-A constituent is very small when t8/5 is between 0.3 and 30 s. The morphology of the M-A constituent obviously changes with the variation of t8/5.As t8/5 increases, tile average width, gross and shape parameter of the M-A constituent increase, while the line density of the M-A constituent decreases.

关 键 词：Laser welding New ultra-low carbon bainitic steel Coarse-grained heat-affected zone MICROSTRUCTURE M-A constituent 

分 类 号：TG456.7[金属学及工艺—焊接]