Fouling-resistant Composite Membranes for Separation of Oil-in-water Microemulsions  

作　　者：王枢 褚良银 陈文梅 

机构地区：[1]School of Chemical Engineering, Sichuan University, Chengdu 610065, China

出　　处：《Chinese Journal of Chemical Engineering》2006年第1期37-45,共9页中国化学工程学报（英文版）

基　　金：Supported by the Trans-century Training Programme Foundation for the Talents by the Ministry of Education of China (No.2002-48).

摘　　要：Fouling-resistant ceramic-supported polymer composite membranes were developed for removal of oil-in-water （O/W） mieroemulsions. The composite membranes were featured with an asymmetric three-layer structure, i.e., a porous ceramic membrane substrate, a polyvinylidene fluoride （PVDF） ultrafiltration sub-layer, and a polyamide/polyvinyl alcohol （PVA） composite thin top-layer. The PVDF polymer was east onto the tubular porous ceramic membranes with an immersion precipitation method, and the polyamide/PVA composite thin top-layer was fabricated with an inteffaeial polymerization method. The effects of the sub-layer composition and the recipe in the inteffaeial polymerization for fabricating the top-layer on the structure and performance of composite membranes were systematically investigated. The prepared composite membranes showed a good performance for treating the O/W microemulsions with a mean diameter of about 2.41μm. At the operating pressure of 0.4MPa, the hydraulic permeability remained steadily about 190L·m^-2·h^-1, the oil concentration in the permeate was less than 1.6mg·L^-1, and the oil rejection coefficient was always higher than 98.5% throughout the operation from the beginning.Fouling-resistant ceramic-supported polymer composite membranes were developed for removal of oil-in-water (O/W) microemulsions. The composite membranes were featured with an asymmetric three-layer structure, i.e., a porous ceramic membrane substrate, a polyvinylidene fluoride (PVDF) ultrafiltration sub-layer, and a polyam-ide/polyvinyl alcohol (PVA) composite thin top-layer. The PVDF polymer was cast onto the tubular porous ceramic membranes with an immersion precipitation method, and the polyamide/PVA composite thin top-layer was fabricated with an interfacial polymerization method. The effects of the sub-layer composition and the recipe in the interfacial po-lymerization for fabricating the top-layer on the structure and performance of composite membranes were systematically investigated. The prepared composite membranes showed a good performance for treating the O/W microemulsions with a mean diameter of about 2.4μm. At the operating pressure of 0.4MPa, the hydraulic permeability remained steadily about 190L?m-2?h-1, the oil concentration in the permeate was less than 1.6mg·L-1, and the oil rejection coefficient was always higher than 98.5% throughout the operation from the beginning.

关 键 词：composite membranes fouling-resistant oil/water separation MICROEMULSION interracial polymerization 

分 类 号：TQ028.8[化学工程]