Thermosensitive Poly(N-isopropylacrylamide-co-acrylonitrile) Hydrogels with Rapid Response  

作　　者：黄健 黄志明 包永忠 翁志学 

机构地区：[1]State Key Laboratory of Polymer Reaction Engineering, Zhejiang University, Hangzhou 310027, China

出　　处：《Chinese Journal of Chemical Engineering》2006年第1期87-92,共6页中国化学工程学报（英文版）

摘　　要：Acrylonitrile (AN) was copolymerized with N-isopropylacrylamide (NIPA) to synthesize thermosensitive hy-drogels, and the on-off switch behavior of poly(NIPA-co-AN) hydrogels with different fraction of hydrophobic compo-nent (AN) was investigated. It is found that the lower critical solution temperature (LCST), the swelling ratio at certain temperature and the reswelling rate of poly(NIPA-co-AN) hydrogels decreased as AN unit fraction in copolymers in-creased. In order to improve the responsive rate of poly(NIPA-co-AN) hydrogels, they were further treated by surface crosslinking using N, N′-methylene bisacrylamide (BIS) as a crosslinking agent. The swelling and deswelling behaviors of these copolymers were compared with those of the untreated hydrogels. The results indicated that the responsive rate of poly(NIPA-co-AN) hydrogel was improved by surface crosslinking. The resulting hydrogels bearing cyano groups with fast response have potential applications in the field of drug-controlled release and immobilization of biomolecules.Acrylonitrile （AN） was copolymerized with N-isopropylacrylamide （NIPA） to synthesize thermosensitive hydrogels, and the on-off switch behavior of poly（NIPA-co-AN） hydrogels with different fraction of hydrophobic component （AN） was investigated. It is found that the lower critical solution temperature （LCST）, the swelling ratio at certain temperature and the reswelling rate of poly（NIPA-co-AN） hydrogels decreased as AN unit fraction in copolymers increased. In order to improve the responsive rate of poly（NIPA-co-AN） hydrogels, they were further treated by surface crosslinking using N, N′-methylene bisacrylamide （BIS） as a crosslinking agent. The swelling and deswelling behaviors of these copolymers were compared with those of the untreated hydrogels. The results indicated that the responsive rate of poly（NIPA-co-AN） hydrogel was improved by surface crosslinking. The resulting hydrogels bearing cyano groups with fast response have potential applications in the field of drug-controlled release and immobilization of biomolecules.

关 键 词：POLYMERIZATION HYDROGEL rapid response 

分 类 号：O621.25[理学—有机化学]