埋弧法精炼技术的应用  

Application of Technology for Submerged Arc Foaming Slag

作　　者：牛四通[1] 成国光[1] 张鉴[1] 佟福生[1] 杨德华 王剑志 梅洪生[1] 杨建川 黎绪炳 

机构地区：[1]北京科技大学冶金系,长城特殊钢公司,江油市宏达冶金辅助材料厂

出　　处：《特殊钢》1996年第2期47-51,共5页Special Steel

摘　　要：在电弧炉还原期的使用结果表明，开发出的埋弧渣产品，能使炉渣高度增大一倍，平均脱Ｓ率为７４．９％，并有一定的脱Ｐ效果。在钢包炉（ＬＦ）上的使用表明，渣厚增大一倍以上；升温速度由１～２℃／ｍｉｎ提高到３～４℃／ｍｉｎ；平均精炼时间节约了１２ｍｉｎ；钢包寿命显著提高；节电３．７ｋＷｈ／ｔ钢；平均脱Ｓ率４５％。The results of application in arc furnace reduction period show that, the submerged arc slag product developed can enable the slag height to increase by more than 100%, the average desulphuring efficiency to get 74.9%,and the phosphorus to decrease in steel. And the results of application of the developed slag in ladle furnace refining show that,the slag height increased two times as against former slag.the heating rate of steelfrom l￣ 2 AC /min to 3--4C/min,the average refining time decreased by 12 minutes,the electric energy consumption decreased by 3. 7 kWh/t and the average desulphuring efficiency was 45%.

关 键 词：泡沫渣 精炼 电弧炉 钢包炉 埋弧渣 

分 类 号：TF769.2[冶金工程—钢铁冶金]