氧化锂对高胶凝性水泥熟料矿物形成的影响  

Effect of Lithia on the Mineral Formation of High Cementing Clinker

作　　者：马素花[1] 沈晓冬[1] 龚学萍[1] 钟白茜[1] 

机构地区：[1]南京工业大学材料科学与工程学院,南京210009

出　　处：《硅酸盐通报》2006年第3期74-77,共4页Bulletin of the Chinese Ceramic Society

基　　金：国家"973"计划重点基础研究(2001CB610701);江苏省"六大人才高峰"资助项目.

摘　　要：研究了Li2O对含硫铝酸钙矿物硅酸盐水泥熟料的易烧性及矿物形成的影响。借助化学分析测定了水泥熟料中游离氧化钙(f-CaO)的含量,用X射线衍射(XRD)分析了熟料矿物组成,采用差热分析(DSC)研究了矿物形成过程。结果表明:生料中掺入少量的Li2O能改善水泥生料的易烧性,促进f-CaO的吸收,促进硫铝酸钙(C4A3S)与硅酸三钙(C3S)的共存。The effect of lithia on the burnability and mineral formation of the clinker containing C4A3S^- was investigated. The f-CaO content, mineral composite and formation process of mineral in the clinker were analyzed respectively by chemical analysis, X-ray diffraction （XRD） and differential scanning calorimetry （DSC）. The results show that adding minor amount of Li2O into the raw material can improve the burnability of raw material , promote the f-CaO absorption and improve the coexistence between calcium sulphoaluminate （C4A3S^-） and tricalcium （C3S）.

关 键 词：氧化锂 硫铝酸钙 硅酸三钙 

分 类 号：TQ172.71[化学工程—水泥工业] TQ172.727[化学工程—硅酸盐工业]