Self-propagating high temperature synthesis of MoSi_2 matrix composites  

作　　者：Akhtar Farid S.H. Islam 

机构地区：[1]Materials Science and Engineering School, State Key Laboratory for Advanced Metals and Materials, University of Science and Technology Beijing, Beijing 100083, China

出　　处：《Rare Metals》2006年第3期225-230,共6页稀有金属（英文版）

基　　金：This project was financially supported by the National Natural Science Foundation of China (No. 50025412)

摘　　要：MoSi2 is presently regarded as the most important material for electrical heating and as one with huge potential for high temperature structural uses. MoSi2 and MoSi2 matrix composites were prepared by self-propagating high temperature synthesis （SHS）. Pure MoSi2 was obtained and a compound of MoSi2 and WSi2was synthesized in the form of predominant solid solution （Mo,W）Si2. By adding aluminum of 5.5 at.% to Mo-Si, the crystal structure of MoSi2 changed into a mixture of tetragonal Cllb MoSi2and hexagonal C40 Mo（Si,Al）2. The （Mo,W）Si2-Mo（Si,Al）2-W（Si,Al）2 composite materials were synthesized by adding aluminum of 5.5 at.% to Mo-W-Si. However, if the amount of the added aluminum was not larger than 2.5 at.%, it did not have any significant effect. SHS is an effective technology for synthesis of MoSi2 and MoSi2 matrix composites.MoSi2 is presently regarded as the most important material for electrical heating and as one with huge potential for high temperature structural uses. MoSi2 and MoSi2 matrix composites were prepared by self-propagating high temperature synthesis （SHS）. Pure MoSi2 was obtained and a compound of MoSi2 and WSi2was synthesized in the form of predominant solid solution （Mo,W）Si2. By adding aluminum of 5.5 at.% to Mo-Si, the crystal structure of MoSi2 changed into a mixture of tetragonal Cllb MoSi2and hexagonal C40 Mo（Si,Al）2. The （Mo,W）Si2-Mo（Si,Al）2-W（Si,Al）2 composite materials were synthesized by adding aluminum of 5.5 at.% to Mo-W-Si. However, if the amount of the added aluminum was not larger than 2.5 at.%, it did not have any significant effect. SHS is an effective technology for synthesis of MoSi2 and MoSi2 matrix composites.

关 键 词：powder metallurgy MoSi2 matrix composites self-propagating high temperature synthesis molybdenumtungsten disilicide molybdenum aluminosilicide 

分 类 号：TB331[一般工业技术—材料科学与工程]