Preparation of nanocrystalline palladium on p-Si by electroless deposition and its photo-electrochemical hydrogen evolution property  

作　　者：YAO Suwei LI He ZHANG Weiguo WANG Hongzhi BEN Yuheng 

机构地区：[1]SUGIYAMA Laboratory of Surface Technology, School of Chemical Engineering and Technology, Tianjin University, Tianjin 300072, China

出　　处：《Rare Metals》2006年第3期241-245,共5页稀有金属（英文版）

基　　金：This work is financially supported by the National Natural Science Foundation of China (No. 50271046) and the Special-ized Research Fund for the Doctoral Program of Higher Education (No. 20030056034)

摘　　要：The Pd-modified p-Si electrode was prepared by means of electroless deposition. The average diameter of Pd nanoparticles was about 80 nm from SEM observations. XRD results showed that the structure of Pd coatings was nanocrystalline. The catalyzing properties of the Pd-modified p-Si electrode for hydrogen evolution under illumination and in dark were studied with the constant current polarization method. The polarization potential for hydrogen evolution reac- tion （HER） of the Pd/p-Si electrode under illumination was 250 mV lower than that in dark, and was 450 mV lower than that of p-Si in dark at the current density of 2.5 mA·cm^-2. The results of electrochemistry impedance spectra （EIS） showed that electrochemistry HER resistance of the modified electrode under illumination decreased from 593.12 to 442.20 Ω·cm^2, and the HER rate increased evidently.The Pd-modified p-Si electrode was prepared by means of electroless deposition. The average diameter of Pd nanoparticles was about 80 nm from SEM observations. XRD results showed that the structure of Pd coatings was nanocrystalline. The catalyzing properties of the Pd-modified p-Si electrode for hydrogen evolution under illumination and in dark were studied with the constant current polarization method. The polarization potential for hydrogen evolution reac- tion （HER） of the Pd/p-Si electrode under illumination was 250 mV lower than that in dark, and was 450 mV lower than that of p-Si in dark at the current density of 2.5 mA·cm^-2. The results of electrochemistry impedance spectra （EIS） showed that electrochemistry HER resistance of the modified electrode under illumination decreased from 593.12 to 442.20 Ω·cm^2, and the HER rate increased evidently.

关 键 词：ELECTROCHEMISTRY Pd-modified p-Si electrode ELECTROLESS hydrogen evolution reaction 

分 类 号：O646[理学—物理化学]