冷轧无取向硅钢50W470铁损的各向异性  

Anisotropy of Iron Loss of Non-Orientation Silicon Steel 50W470

作　　者：孙述利[1] 张敏刚[1] 郭东城[1] 姚力[2] 宋文军[2] 

机构地区：[1]太原科技大学材料学院,太原030024 [2]太原钢铁(集团)有限公司,太原030003

出　　处：《特殊钢》2006年第4期34-35,共2页Special Steel

基　　金：太原科技大学青年基金项目资助(200510)

摘　　要：对成分(％)为0．003C、1．46Si、0．38Al的0．5 mm冷轧无取向硅钢板进行夹杂物、组织和织构的测定与分析。分析结果表明,试样铁损各向异性为7．56％-11．01％;合理提高无取向硅钢50W470热轧时的终轧温度,有利于提高织构组分密度;同时延长冷轧板的连续退火时间,以利于位向晶粒充分长大,从而减少铁损的各向异性。The inclusion, structure and texture of 0.5 mm cold rolled sheet of non-orientation silicon steel - 0.003C, 1.46Si, 0.38M have been tested and analyzed. The analyzed results showed that difference in anisotropy of iron loss of sample was 7.56%- 11.01%. Reasonably increasing finishing rolling temperature of non-orientation silicon steel 50W470 is available to increase density of texture component and prolonging continuous annealing time of cold rolling sheet is available to enough crow of directional grain, thus the anisotroov of iron loss reduces.

关 键 词：冷轧无取向硅钢 各向异性 热轧终轧温度 退火时间 

分 类 号：TG335.12[金属学及工艺—金属压力加工]